Electronics Forum | Thu Aug 01 13:10:46 EDT 2002 | johnw
Chris, I don't know what machine your using, but we're also playing with one at the moment and don't see any problems with micro solderballing as far as I'm aware (I'll double check tomorrow thou!) We're using Kester 977 with it and don't have a pro
Electronics Forum | Mon Apr 25 11:24:31 EDT 2005 | Daan Terstegge
I have a question about inspection, touch-up, and how far you need to go to get a product that meets the required IPC-spec. According to some reports (i.e. "New Study Reveals Component Defect Levels" by Stig Oresjo of Agilent) the average defect leve
Electronics Forum | Sun May 02 11:53:43 EDT 1999 | Chrys Shea
| | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | My question's are really : | | how is the
Electronics Forum | Sun May 02 19:09:46 EDT 1999 | JohnW
| | | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | | | My question's are really : | |
Electronics Forum | Wed May 05 10:57:25 EDT 1999 | Kevin Hussey
| | | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | | | My question's are really : | |
Electronics Forum | Sat May 08 07:41:00 EDT 1999 | wayne sanita
hello, i have been using up-78 ultraprint for over a year now. at first we were getting lots of solder balls mainly on 0805's. this happened with all paste we used, too much solder under component leads. i have been using apertures reduced 10% homepl
Electronics Forum | Tue Sep 21 17:24:58 EDT 1999 | John Thorup
| | | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | | | thanks | | | | | | | We use 6 mil lasercu
Electronics Forum | Wed Sep 22 21:12:16 EDT 1999 | se
| | | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | | | thanks | | | | | | | We use 6 mil lasercu
Electronics Forum | Thu Aug 05 12:20:06 EDT 1999 | John Thorup
| | | | | | | | | | | | | | | Hello, | | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem
Electronics Forum | Mon Jun 28 22:02:13 EDT 1999 | Dave F
| Hey there gang, how's it going ? | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's ar