Electronics Forum | Tue May 26 16:35:53 EDT 1998 | Ryan Jennens
| | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized
Electronics Forum | Fri Jul 29 16:20:57 EDT 2016 | davef
"ALPHA® EF-2210 is VOC-free, halide-free, rosin/resin-free, low solids no-clean flux which provides the highest activity of any VOC-free Bellcore SIR compliant flux for defect-free soldering. "[2016 Alpha Assembly Solutions] I assume that you're tal
Electronics Forum | Wed May 27 15:09:30 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Wed May 27 09:56:39 EDT 1998 | Chrys
| | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localize
Electronics Forum | Thu Feb 16 13:21:24 EST 2006 | Bill C
Hi Russ, Thanks for the reply. No this is 856, I sprayed some on boards just to try it out and noticed it dries very quickly also but if its soldered right away as would be the case in the machine, it's fine. I believe I tried some 857 and found th
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Wed May 27 15:54:09 EDT 1998 | Chrys
| | | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not loca
Electronics Forum | Mon May 17 16:34:25 EDT 2004 | pjc
I am an equip mfrs rep. I took a customer to my wave solder principal's factory to run their boards on a wave with no-Pb alloy, (Sn96.5 Ag3.0 Cu0.5) in air environment. The results were excellent with pot temp of 263C (505F). Their boards are low to
Electronics Forum | Fri Dec 15 08:00:57 EST 2000 | Pete B
John, We regularly wave solder electroless silver finished boards (Alpha Level)with mixed SMD and through hole parts and do not have any problems. We have changed a number on PCB's from HASL to electroless silver, mainly for the benefits at SMD whe
Electronics Forum | Mon Jul 20 20:58:54 EDT 1998 | Dave F
| | Dave: | Wayne is correct with his analysis of ultrasonic spraying - we also use Sonoteks. However, your post didn't ask for a different system, just a clarification regarding your problem. What type of flux system are you currently using - s