Electronics Forum | Fri May 31 10:35:46 EDT 2002 | dason_c
I think that the IPC spec only apply to the MSD. I had a paper from Lucent and forwarded by Francois Monette, please aware that the first 2 hours, the moisture doesn't bake out from the assembly/component and result show that it is increase the weigh
Electronics Forum | Thu Aug 05 13:37:28 EDT 2004 | davef
Baking your boards will redue the amount of OSP on the board. If you use the boards quickly, you probably will not have a problem with baking [and don't bake too long]. Why do you want bake this board?
Electronics Forum | Thu Aug 05 05:28:03 EDT 2004 | Bryan
There 's one thing I'm not sure...For the OSP board finish whether we could bake and then store this kind of PCB?or whether once we opened the vacumm package of OSP board and then we can't bake it ? Thanks Bryan
Electronics Forum | Fri Aug 15 09:48:10 EDT 2003 | davef
First, what do you mean by "mishandled OSP" boards? Second, we don't like to bake our OSP boards, because of the potential to degrade the coating. Why do you want to bake these boards? Third, why not paste-up a board, reflow it, and assess the sol
Electronics Forum | Tue Aug 26 07:39:54 EDT 2008 | evtimov
thanks. i was looking at the silicon horizon > controller for the toaster. just to help keep the > temp constant since i can not watch it all night! this way of baking is good just for small quantities. If you want to built a lot of boards, you b
Electronics Forum | Mon May 17 13:21:45 EDT 2021 | SMTA-64387881
PWB Bake out or other elevated temperture processes can cause issues with oxidation of that Nickel layer. The gold porosity can vary from batch to batch, but also process changes can contribute. Are you baking the boards or have previous reflow pro
Electronics Forum | Thu Aug 05 16:15:18 EDT 2004 | pjc
Are you considering baking due to moisture exposure? Not all OSPs are created equal. I would check with your PWB fabricator about dry times and effects on their OSP finish. After you get it, I'd still try just one PWB for bake-dry out and check solde
Electronics Forum | Tue Feb 20 21:43:24 EST 2007 | sbkwak
Is there any technical reason why OSP finished PCB should not be baked? Your advice will be very much appreciated
Electronics Forum | Mon Jan 08 10:41:50 EST 2007 | jaime39
If you bake the boards at 125 degrees celcius for about 4 hours it should work. I would also suggest that you talk to the PCB supplier to take care of this baking for you. NOTE: PCB�s with an Entek or any other type of OSP finish should not be baked.
Electronics Forum | Fri Aug 06 10:07:50 EDT 2004 | blnorman
OSP has limited elevated temperature exposure capability. Couple that with the fact that solvents (IPA in particular) will remove the OSP. The more material you loose the higher the chances for pad oxidation. We ran an experiment with board washin