Electronics Forum | Wed Aug 04 16:49:24 EDT 2004 | jim_bob
Regarding Lead Free component finishes, vendors are zeroing in on matte tin plating as the finish of choice. What test are performed, to determine if a finish is "matte" type (vs. non-matte)?
Electronics Forum | Thu Aug 05 14:45:03 EDT 2004 | davef
Bright vs matte tin is fairly easy, but there's a s whole bunch of alternatives, beyond those two choices. So, no, not that we know.
Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker
We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had
Electronics Forum | Wed Aug 05 07:46:46 EDT 1998 | Earl Moon
| We have mixed to negative feelings about Omikron, but I beileve it is due to problems with the board fabricator rather than the process itself. When done properly, our Omikron boards have had very good solderability. However, we have had several
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Wed Sep 19 16:02:14 EDT 2001 | fcouture
Pad Metallurgy Used: >Is your question about this targeting the current industry capability of using tin plating technology on such small >pad dimensions? Actually I should have asked for tin/lead plating (HASL) and yes it's to have an idea on capab
Electronics Forum | Wed Jul 29 22:50:17 EDT 1998 | Dave F
| We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone ha
Electronics Forum | Wed Sep 19 14:23:31 EDT 2001 | jschake
Pad Metallurgy Used: Copper OSP pads were used for all of the results that I have been reporting. The same design test boards with Nickel/Gold pads are available and awaiting further assembly tests. I will consult with a board technology and metall
Electronics Forum | Fri Nov 10 17:44:48 EST 2000 | Dave F
In response to your questions: Is the embrittlement from excess gold in lead / tin solder connections bad? It can be vereeee bad. Does it affect all plating processes the same? Give us a break and read the SMTnet Archives, for instance: BGA prob
Electronics Forum | Fri Sep 21 14:45:36 EDT 2001 | jschake
I asked several people their opinion of HASL 0201 pads and there was no positive feedback whatsoever. The most common concern was the domed/convex shape of the pad finish that would result in aperture gasketing problems, which you may already have e