Electronics Forum | Fri May 26 14:03:52 EDT 2000 | GP
I have a problem on fine pitch SMT connector reflow. The board size is 18" x 12" with 8 layers FR4 material and emersion gold finishing. All the other components include 0603 on the board are reflow very well, except 20 mil pitch SMT connectors. The
Electronics Forum | Tue Dec 11 11:59:00 EST 2012 | sarason
The issue is surface tension around the connector. Your tip needs to have more surface tension than the pins of the connector as it forms a cluster when being soldered. When I used to solder superfine connectors with a metcal iron it had a horses hoa
Electronics Forum | Mon Dec 10 13:26:40 EST 2012 | dyoungquist
We are using our selective solder machine to solder a backplane with sixteen (16) 4x48 pin 0.080" connectors. Our first pass yield is about 85% meaning that 85% of the connectors come out with no bridges. Not quite as fine pitch as your connector a
Electronics Forum | Fri Dec 07 13:31:09 EST 2012 | kenkay
We had a similar issue and it was fixed by trimming the connector so there was barely enough lead protrusion through the board to show a discernible lead. We had to get a special plate and small machine to cut the connectors, but we haven’t had a bri
Electronics Forum | Tue Feb 26 14:39:19 EST 2013 | eniac
Hi, guys. Does anyone use a EBSO selective soldering machines? Can you write your parameters for two rows connector? Thx!
Electronics Forum | Fri Dec 07 02:53:26 EST 2012 | beta
no expert but would using a smaller diameter nozzle help in anyway?
Electronics Forum | Fri Dec 07 02:55:24 EST 2012 | aj
I am no expert but would using a smaller nozzle help in anyway?
Electronics Forum | Wed Dec 12 16:16:39 EST 2012 | tombstonesmt
Nitrogen at nozzle supply is at around 47.5cfh.
Electronics Forum | Wed Dec 19 10:33:58 EST 2012 | emeto
I had a connector like this and here is my recommendation: 1. Flux type(I like better alchohol based flux than water based) 2. Try higher soldering speed(when I say higher I mean several times higher) Goodf Luuck!
Electronics Forum | Thu Sep 07 10:39:34 EDT 2006 | vicknesh28
Can u elaborate on the bad plating? Have u had any experience on this before? The component has 90/10 Tin lead plating