Electronics Forum | Mon Mar 20 09:24:38 EST 2000 | John Sipper
1. Spec references for max allowable untinned gold near glass seal and case body? 2. Low cost mechanical dip system to facilitate tinning of DIP parts. (Low volume; currently using hand solder iron techniques to allow for max coverage without bridg
Electronics Forum | Wed Aug 06 16:35:31 EDT 2003 | Carol
This is an old topic, but keeps coming up. Solderability and reliability issues with SMT gold plated terminations when used with tin/lead solder paste/hassle finish PWB. I need to know which standard (mil, IPC, J-STD??) tells you all about the probl
Electronics Forum | Tue Mar 21 20:25:30 EST 2000 | Dave F
John: What�s the matter? Free gold � good thing for you, bad thing for your supplier. :^) Pre-tinning of gold plated leads is important to: � Prevent gold embrittlement of the solder joint � Determine if the leads are solderable prior to assembly (
Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec
Electronics Forum | Mon Apr 14 09:39:49 EDT 2003 | davef
Consider: * Sn has a higher melting point than Pb. So the liquidous temperature of this new, non-Sn63 is going to be higher than 183*C. What was the thermal recipe measured on this solder connection? * Next thing we'd do is take problem devices and
Electronics Forum | Fri May 31 08:51:09 EDT 2002 | zanolli
Hello Dave, As related to connector mating interface, fretting corrosion is the oxidation of the contact points, causing high resistance across the interface. Fretting corrosion is caused my micromotions in the interface exposing the metalized conta
Electronics Forum | Thu Jan 27 14:49:53 EST 2000 | Glenn Robertson
Tuan - One of the reasons I suggested pre-tinning (aside from the negative effects of Gold on appearance and reliability) is the known slower wetting of Sn/Ag and Sn/Cu alloys as compared to Sn/Pb. If you don't have to be Lead-free, the high Lead
Electronics Forum | Wed Jan 26 14:33:47 EST 2000 | Glenn Robertson
Tuan - How about Sn/0.7Cu? It's M.P. is 227 and it's readily available. If the leads are Gold plated you might consider pre-tinning them. If you need a higher temp alloy any of the major solder companies can help - I suggets you start with Ind
Electronics Forum | Tue Dec 10 05:03:58 EST 2002 | praveen
We are having solder fillet finish issue. The solder looks like rough solder on the connector leads .The plating of the leads is Nickel (99.9% purity) and the PCB plating is imersion gold. I have tried fine tuning my reflow profiles an have used N2 i
Electronics Forum | Tue Dec 10 20:42:43 EST 2002 | davef
Vijay, Sounds like you're not spending enough time at liquidous plus 20*C. And you need to stay there for 5 to 10 seconds. I know, I know. We have used bucketsful of WS609 over the years. See, as you say, the melting point of your solder alloy