Electronics Forum | Mon Jul 19 12:37:15 EDT 1999 | Wolfgang Busko
| | | | | Hi, SMTASSY | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | First, we do not do real series produktion, only prototyping up to som
Electronics Forum | Tue Jul 20 05:29:14 EDT 1999 | Wolfgang Busko
| | | | | | | | Hi, SMTASSY | | | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | | First, we do not do real series produktion, only prototypi
Electronics Forum | Wed Nov 17 09:28:40 EST 1999 | Steve Z
Hello, I am new to the SMT area and I need to know what a "good" vapor phase reflow profile should look like. The fluids we are using have a BP of 45 C and 219 C. Thanks,
Electronics Forum | Fri Nov 19 05:12:21 EST 1999 | Graham Naisbitt
Steve, If you can get me your snail-mail address, I will send you some latest information. We actually have a totally new system called Delta 5. It is Condensation Soldering rather than Vapour phase, the difference being that we solder in an air ti
Electronics Forum | Mon Jul 19 11:11:18 EDT 1999 | Wolfgang Busko
| Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still t
Electronics Forum | Mon Jul 19 11:50:47 EDT 1999 | Mario
| | Hi, SMTASSY | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | First, we do not do real series produktion, only prototyping up to sometimes 20 uni
Electronics Forum | Wed Mar 12 15:26:46 EDT 2014 | dan_ems
Hello, in my SMT process I have some problems with the solderability (look like dewetting) on a PCB with finish HASL Lead Free with a composition that is melt at 230 degree Celsius. My oven is with vapor phase and the peak temperature is 230 degre
Electronics Forum | Thu Mar 13 14:12:31 EDT 2014 | davef
You're creating a new alloy on the surface of your board. The alloy will have a melting point determined by the constituent metals of the alloy. Your alloy consists of: * Lead-free HASL solderability protection on the board * Lead-free solder paste *
Electronics Forum | Wed Jan 30 12:37:49 EST 2002 | jax
nifhail, In a nutshell: Vapor-phase reflow is a process that uses a fluid with a selected boiling point. As condensation of the hot vapor occurs on a cool assembly the assembly's temperature is rapidly raised to match the temperature of the vapor.
Electronics Forum | Wed Jan 30 17:48:31 EST 2002 | davef
Expanding on a previous poster's comments ... Vapor Phase Soldering. A solder reflow technology that uses a heated solvent to melt the solder. Buried deep in the recesses of the SMTnet Library is �Terms & Definitions�. We started using vapor phas