Technical Library | 2019-05-01 23:18:27.0
Moisture can accelerate various failure mechanisms in printed circuit board assemblies. Moisture can be initially present in the epoxy glass prepreg, absorbed during the wet processes in printed circuit board manufacturing, or diffuse into the printed circuit board during storage. Moisture can reside in the resin, resin/glass interfaces, and micro-cracks or voids due to defects. Higher reflow temperatures associated with lead-free processing increase the vapor pressure, which can lead to higher amounts of moisture uptake compared to eutectic tin-lead reflow processes. In addition to cohesive or adhesive failures within the printed circuit board that lead to cracking and delamination, moisture can also lead to the creation of low impedance paths due to metal migration, interfacial degradation resulting in conductive filament formation, and changes in dimensional stability. Studies have shown that moisture can also reduce the glass-transition temperature and increase the dielectric constant, leading to a reduction in circuit switching speeds and an increase in propagation delay times. This paper provides an overview of printed circuit board fabrication, followed by a brief discussion of moisture diffusion processes, governing models, and dependent variables. We then present guidelines for printed circuit board handling and storage during various stages of production and fabrication so as to mitigate moisture-induced failures.
Technical Library | 2024-01-08 18:36:01.0
The following aims lie behind the investigations described: The circuit board is an integrated structure made of metal and plastic. Like most integrated components enclosed in plastic, it absorbs water. When it is rapidly heated as, for example, in soldering technology temperature processes, it is a well known fact that the water will evaporate abruptly, leading to destruction. It is therefore essential that the circuit board be dried before these soldering processes. Circuit board manufacturers are extremely hesitant at providing instructions on drying their circuit boards. Information from the ZVEI [1] should also be regarded critically. The cardinal problem is the high temperature which is recommended for baking. If this is applied, the result is often de-lamination and distortion of the circuit boards. Corrosion and the formation of intermetallic phases of the metallic surfaces are also to be expected. The following investigates whether gentle drying at 45°C or 60°C and at low relative humidity achieves the same result as baking at high temperatures. The industry provides novel dry cabinets which are suitable for rapid drying at relative humidities below one percent.
Technical Library | 2016-05-12 16:29:40.0
Advances in miniaturized electronic devices have led to the evolution of microvias in high density interconnect (HDI) circuit boards from single-level to stacked structures that intersect multiple HDI layers. Stacked microvias are usually filled with electroplated copper. Challenges for fabricating reliable microvias include creating strong interface between the base of the microvia and the target pad, and generating no voids in the electrodeposited copper structures. Interface delamination is the most common microvia failure due to inferior quality of electroless copper, while microvia fatigue life can be reduced by over 90% as a result of large voids, according to the authors’ finite element analysis and fatigue life prediction. This paper addresses the influence of voids on reliability of microvias, as well as the interface delamination issue.
| 1 |