Technical Library | 1999-08-27 09:27:10.0
Conformal coating is a material that is applied to electronic products or assemblies to protect them from solvents, moisture, dust or other contaminants that may cause harm. Coating also prevents dendrite growth, which may result in product failure. This paper will discuss the variables that affect the application of conformal coatings, and review in detail those variables that impact the process of selective coating of printed circuit boards.
Technical Library | 2024-09-02 21:02:46.0
In conformal coating, there are several mechanisms that cause failure of printed circuit boards (PCBs). In a series of technical bulletins SCH will examine the common failure mechanisms in conformal coating including capillary flow, delamination, cracking, loss of adhesion, dewetting, corrosion, orange peel, pinholes, bubbles and foam.
Technical Library | 2021-08-11 01:00:37.0
Conformal coatings and potting materials continue to create issues for the electronics industry. This webinar will dig deeper into the failure modes of these materials, specifically issues with Coefficient of Thermal Expansion (CTE), delamination, cracking, de-wetting, pinholes/bubbles and orange peel issues with conformal coatings and what mitigation techniques are available. Similarly, this webinar will look at the failure modes of potting materials, (e.g Glass Transition Temperature (Tg), PCB warpage, the effects of improper curing and potential methods for correcting these situations.
Technical Library | 2013-10-13 10:22:48.0
There are numerous factors which directly affect the conformal coating process to greater or lesser degrees. Those which have major impacts irrespective of the substrate / PCB and assemblies include choice of coating material and method of application. Whether conformal coating boards by dip, robot, batch spray or brush methods the viscosity of the coating is a critical factor in the overall process control.
Technical Library | 2011-01-13 17:37:55.0
The tin whisker failures investigated in this paper were found on functional RoHS-compliant hardware. The samples were not conformal coated. This paper will document the conditions associated with the whisker formation under the following conditions; tin
Technical Library | 2020-01-01 17:06:52.0
The majority of electronic failures occur due to thermally induced stresses and strains caused by excessive differences in coefficients of thermal expansion (CTE) across materials.CTE mismatches occur in both 1st and 2nd level interconnects in electronics assemblies. 1st level interconnects connect the die to a substrate. This substrate can be underfilled so there are both global and local CTE mismatches to consider. 2nd level interconnects connect the substrate, or package, to the printed circuit board (PCB). This would be considered a "board level" CTE mismatch. Several stress and strain mitigation techniques exist including the use of conformal coating.
Technical Library | 2017-12-11 22:31:06.0
Typical printed circuit board assemblies (PCBAs) processed by reflow, wave, or selective wave soldering were analysed for typical levels of process related residues, resulting from a specific or combination of soldering process. Typical solder flux residue distribution pattern, composition, and concentration are profiled and reported. Presence of localized flux residues were visualized using a commercial Residue RAT gel test and chemical structure was identified by FT-IR, while the concentration was measured using ion chromatography, and the electrical properties of the extracts were determined by measuring the leak current using a twin platinum electrode setup. Localized extraction of residue was carried out using a commercial C3 extraction system. Results clearly show that the amount and distribution of flux residues are a function of the soldering process, and the level can be reduced by an appropriate cleaning. Selective soldering process generates significantly higher levels of residues compared to the wave and reflow process. For conformal coated PCBAs, the contamination levels generated from the tested wave and selective soldering process are found to be enough to generate blisters under exposure to high humidity levels.