Technical Library | 2019-07-10 23:36:14.0
Pockets of gas, or voids, trapped in the solder interface between discrete power management devices and circuit assemblies are, unfortunately, excellent insulators, or barriers to thermal conductivity. This resistance to heat flow reduces the electrical efficiency of these devices, reducing battery life and expected functional life time of electronic assemblies. There is also a corresponding increase in current density (as the area for current conduction is reduced) that generates additional heat, further leading to performance degradation.
Technical Library | 2018-04-27 13:23:31.0
When performing BGA component rework, it is important to know the actual heat that is coming out of the top and bottom heaters. This will be critical in setting up accurate heat profiles. Monitoring your heat output will also keep you aware of your heaters performance so that you will know when the heaters need to be replaced.
Technical Library | 2014-10-23 18:10:10.0
The functional reliability of electronic circuits determines the overall reliability of the product in which the final products are used. Market forces including more functionality in smaller components, no-clean lead-free solder technologies, competitive forces and automated assembly create process challenges. Cleanliness under the bottom terminations must be maintained in harsh environments. Residues under components can attract moisture and lead to leakage currents and the potential for electrochemical migration (...) The purpose of this research study is to evaluate innovative spray and soak methods for removing low residue flux residues and thoroughly rinsing under Bottom Termination and Leadless Components
Technical Library | 2017-07-20 15:18:15.0
As electronic devices increase functionality in smaller form factors, there will be limitations, obstacles and challenges to overcome. Advances in component technology can create issues that may have time delayed effects. One such effect is device failure due to soldering residues trapped under bottom terminated components. If the residues trapped under the component termination are active and can be mobilized with moisture, there is the potential for ion mobilization causing current leakage.
Technical Library | 2015-07-14 13:19:10.0
Bottom terminated components (BTC) are leadless components where terminations are protectively plated on the underside of the package. They are all slightly different and have different names, such as QFN (quad flat no lead), DFN (dual flat no lead), LGA (land grid array) and MLF (micro lead-frame. BTC assembly has increased rapidly in recent years. This type of package is attractive due to its low cost and good performance like improved signal speeds and enhanced thermal performance. However, bottom terminated components do not have any leads to absorb the stress and strain on the solder joints. It relies on the correct amount of solder deposited during the assembly process for having a good solder joint quality and reliable reliability. Voiding is typically seen on the BTC solder joint, especially on the thermal pad of the component. Voiding creates a major concern on BTC component’s solder joint reliability. There is no current industry standard on the voiding criteria for bottom terminated component. The impact of voiding on solder joint reliability and the impact of voiding on the heat transfer characteristics at BTC component are not well understood. This paper will present some data to address these concerns.
Technical Library | 2013-07-25 14:02:15.0
Bottom-termination components (BTC), such as QFNs, are becoming more common in PCB assemblies. These components are characterized by hidden solder joints. How are defects on hidden DFN joints detected? Certainly, insufficient solder joints on BTCs cannot be detected by manual visual inspection. Nor can this type of defect be detected by automated optical inspection; the joint is hidden by the component body. Defects such as insufficients are often referred to as "marginal" defects because there is likely enough solder present to make contact between the termination on the bottom-side of the component and the board pad for the component to pass in-circuit and functional test. Should the board be subjected to shock or vibration, however, there is a good chance this solder connection will fracture, leading to an open connection.
Technical Library | 2019-07-24 23:55:32.0
Voiding is a key concern for components with thermal planes because interruptions in Z-axis continuity of the solder joint will hinder thermal transfer. When assembling components with solder paste, there is a high propensity for voiding due to the confined nature of the solder paste deposits under the component. Once reflowed, many factors contribute to the amount of voiding in a solder joint such as the reflow profile, designs of the component, board and stencil, and material factors. This study will focus on the solder paste alloy and flux combination as well as profile and board surface finishes.
Technical Library | 2023-11-20 17:30:11.0
Summary for today 1. Electronic component inspection and failure analysis. 2. Component counting and material management. 3. Reverse engineering. 4. Counterfeit detection. 5. Real-time defect verification. 6. Computed tomography (CT) techniques and how to differentiate between 2D, 2.5D, and 3D x-ray inspection. 7. Design for manufacturing (DFM) and design for x-ray inspection (DFXI). 8. Voids, bridging, and head-in-pillow failures in bottom terminated components (BTC). 9. Artificial Intelligence and x-ray inspection
Technical Library | 2017-02-16 16:53:49.0
This experiment considers the reliability of a variety of different electronic components and evaluates them on 0.200” power computing printed circuit boards with OSP. Single-sided assemblies were built separately for the Top-side and Bottom-side of the boards. This data is for boards on the FR4-06 substrate.This paper was originally published by SMTA in the Proceedings of SMTA International.
Technical Library | 2023-09-18 14:10:01.0
As with many advancements in the electronics industry, consumer electronics is driving the trends for electronic packaging technologies toward reducing size and increasing functionality. Microelectronics meeting the technology needs for higher performance, reduced power consumption and size, and off the- shelf availability. Due to the breadth of work being performed in the area of microelectronics packaging/components, this report limits it presentation to board design, manufacturing, and processing parameters on assembly reliability for leadless (e.g., quad flat no-lead (QFN) or a generic term of bottom termination component (BTC)) packages. This style of package was selected for investigation because of its significant growth, lower cost, and improved functionality, especially for use in an RF application.