Electronics Forum | Thu Oct 06 06:55:02 EDT 2005 | marcusx
We use chrome bowls to drain ours we have done it many times. They work like champ. I have never used the drain spout we just laddle it out. We are using the SN100C here, it is fanatastic. Quite a few process consideration must be made in order to ge
Electronics Forum | Thu Oct 27 08:13:36 EDT 2005 | smtnet21
Is there any engineer who have experience for changing the Juki KE740 language convert ? (English to Japanese, or Japanese to English).. I'd like to change the language to English from Japanese (System version is 5.30C and vision VCS version is 01-0
Electronics Forum | Wed Nov 02 08:21:45 EST 2005 | chunks
Yes, I agree, manual cleaning is not a solution, but does tell you you need to clean the stencil. You should have your stencil cleaner repaired and take that question mark away. Once all the question marks are goen you should be left with an answer
Electronics Forum | Wed Nov 02 15:30:50 EST 2005 | JW
We have demo'ed the Niton and the Innov-X Systems' units. Prices quoted to us were exactly as Ken had mentioned. Serious Ouch but the situation I mentioned sure helped sway management towards a purchase. In addition to contracting spare time with t
Electronics Forum | Wed Nov 02 04:28:58 EST 2005 | Simon
Hi James, I have worked in many SMT sites and this is not an uncommon practice. It is true that print deposit consistency will improve after the first few prints as the aperture walls become lubricated, but with modern stencils/paste and a well-desig
Electronics Forum | Wed Nov 02 01:24:07 EST 2005 | arnold
we are encountering a problem on our production. after dipping a copper wire AWG#30 to a leadfree solder the wire becom thinner and easily to break. does the leadfree soler has the capability to weaken the wire (lessen the diameter)after dipping to l
Electronics Forum | Wed Nov 02 22:06:54 EST 2005 | davef
Slaine, our intuition is the same as yours [that 100Sn should dissolve the copper faster than other solders]. Bob Gilbert's FCT data shows otherwise. Look here: http://www.fctassembly.com/newsltr/2004/0804/Aug04.htm
Electronics Forum | Wed Nov 02 14:45:26 EST 2005 | chunks
Here's the info on Gel Flex: http://www.adhesivesmag.com/CDA/ArticleInformation/products/BNPProductItem/0,2109,120109,00.html http://www.speedlinetech.com/docs/Gel-FlexBrochure.pdf#search='Gel%20flex' I agree, the Grid Loc was not all it was crake
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Wed Nov 02 12:41:07 EST 2005 | Tapesplice.com
Tape Splicer and Tape Splicing Products for splicing a seamless reel of SMD Components. Tape Splicing increases throughputs and yields by 15-20%. We also manufacture Antistatic Clean Room Lab Coats, Clean Room Coveralls, ESD Grounding Straps, Cleanro