Electronics Forum | Wed Feb 05 05:29:33 EST 2003 | Rajinder Sharma
If you are facing problem of craked capacitor only after breaking of the panel into individual PCB's, this may be due to stress being generated on the capacitors terminals. The stress may be due excess pressure being applied on the panel for breaking
Electronics Forum | Wed Feb 05 09:11:05 EST 2003 | davef
Here is some talk about MLC capacitor flex cracking...what happens with depanelizing: http://www.kemet.com/KEMET/web/homepage/kechome.nsf/vapubfiles/f2106/$file/f2106.pdf Here are some other files on breaking capacitors: http://www.avxcorp.com/doc
Electronics Forum | Wed Feb 05 11:38:46 EST 2003 | Stephen
Don't forget placement. I"ve seen chips broken when they are being placed because they were thicker than the parts data used for them. This is not an issue on Panasonic machines because they measure the thickness of parts but I have seen it happen
Electronics Forum | Sat Feb 15 06:40:14 EST 2003 | Hans Koerner, Germany
It is a serius problem with that mulilayer ceramic caps! In automotive applications you have to use 2 in series for one single cap. During depanelizing you create a mechanically wave in the board, so 3.. 4 mm. Best way is not to do such a wrong desig
Electronics Forum | Wed Feb 05 11:31:40 EST 2003 | lloyd
The grease to use is DAPHNE EPONEX M No. 1 as you would expect it is made by an oriental company (IDEMITSU KOSAN). Sanyo recommend that this procedure should only be carried out by trained personnel, so it may be worth giving them a ring before you s
Electronics Forum | Wed Feb 05 10:31:38 EST 2003 | bpan
Hello Everyone, Is anyone out there building smt boards that have plated through vias directly located through the pads. We are seeing some of these designs and the soldering is very poor because the solder is flowing through the via. We think that w
Electronics Forum | Wed Feb 05 21:05:38 EST 2003 | davef
Iman On your situation: As an earlier poster stated, your options are limited to opening you stencil aperture to compensate for the paste lost to the via. On your designer's belief that "it helps in heat dissipation": Could be true, but: * Hole wil
Electronics Forum | Thu Feb 06 13:57:01 EST 2003 | D. Brian Davis
I need some feedback on aqueous cleaners. We currently use a Unit Design batch cleaner. We will be looking to upgrade our board washing process and batch sizes in the near future. I am looking for user info. on the advantages/disadvantages to using b
Electronics Forum | Fri Feb 07 09:27:07 EST 2003 | davef
For all of the ranting about "sales-types" using the forum inappropriately, it's nice that some of those types get IT. So if you rant when people behaving poorly, then you must praise people when perform well. This is over-due. Hats off to Mike,