Electronics Forum | Tue Mar 07 21:19:50 EST 2000 | Van Hoang Dinh
I have few problems below, 1.I had problem with clean glue stencil at the midle of the process and after the process. 2.Very hard to Fix the bridging on the (close pin) connectors through the wave. Anyone can help on this. Thanks Van
Electronics Forum | Wed Jan 17 13:58:19 EST 2001 | davef
Yano what else is nice about using IE, as compared to using NN? The title of a thread changes color after you select it and then move on to another thread. Cool!!!! Boy, I wish it worked that way in NN!!!!
Electronics Forum | Tue Jan 16 21:00:11 EST 2001 | davef
Two good sources of information are: 1 IPC-7525 Stencil Design Guidelines 2 SMTnet fine Archives [once the guys get them back up and running after the conversion is complete]
Electronics Forum | Wed Feb 14 16:03:54 EST 2001 | lileubie
Do you have a stencil wipe step after every six boards? If so, the wipe either automatic or manual needs to be optimized. Either less solvent or more time for the solvent to evaporate off.
Electronics Forum | Tue Feb 27 22:04:45 EST 2001 | hany_khoga
Dear all: I need to know why do I find a lot of solder balles every where on the solder side of my assemblies after coming out of the wave solder machine. How can I avoid this? Thanks Hany
Electronics Forum | Fri Mar 02 15:52:19 EST 2001 | jagman
This happens to be after the water wash process. These are Burn-In boards so an SMT epoxy is used prior to wave. The flux used is Kester 2331ZX. Would using a thinner cause this to occur? The residue is all over the board. Thanks.
Electronics Forum | Thu Mar 08 16:02:18 EST 2001 | gsmguru
Have you considered a different solderpaste ? A different flux chemistry may help. The metals content wouldn't have to change. Just go after a slightly more aggressive flux.
Electronics Forum | Tue Jun 13 12:00:15 EDT 2000 | Brian Larson
How long and at what temperature to you bake through-hole boards for moisture? I am getting blow holes after the wave solder. Everything points to the drilling of the board, but I need to prove that it is not moisture.
Electronics Forum | Wed May 02 13:59:20 EDT 2001 | kt
Can anyone tell me what they think is the main cause of excessive solder at the end of the lead after wave. These are not solder peaks as if the leads were cold. It is a well wetted ball of solder on end of the lead. Also, some times you see excessiv
Electronics Forum | Sun May 13 21:02:34 EDT 2001 | djarvis
Gary, You're not trying to clean these boards with Iso or other solvents after using no-clean solder paste? That'll do it.