Electronics Forum | Thu Jul 20 12:59:52 EDT 2000 | Mike McMonagle
Bob, I attended your PIHR workshop at Nepcon a few years back. At the risk of making a shameless plug, I must say that the presentation and the materials used were some of the best I have seen in my many (20+) years in the industry. The video that is
Electronics Forum | Wed Sep 01 12:26:32 EDT 1999 | Jae Hinson
To aid in heat dissipation of our PCB, we would like to try having copper fill areas on the board that are hot air levelled and not covered with solder resist. Then, when the board is reflowed, solder paste would be applied and then solder. Has anyon
Electronics Forum | Thu Jan 21 17:07:16 EST 1999 | ed zamborsky
I've had alot of success with the solder pastes from ESP in Rhode Island. They have great shelf life and are easy to print | I'm currently planning to do an evaluation of RMA flux solder pastes for mil type applications. Does anyone have any suggest
Electronics Forum | Fri Jul 24 07:08:43 EDT 1998 | Wayne
Scott: We all understand your situation and I would think have been there ourselves, but just not too sure how posting it on the forum can be of any help in solving the situation. If you are venting then maybe it worked, but there has to be a more di
Electronics Forum | Wed Aug 29 20:48:09 EDT 2001 | Jones
I know this is not the answer to your question but it may help until you get the right cleaning process in place. I have found that kneading the paste with 3-4 double strokes during the first print has aided in bring our defective ppm down somewhat.
Electronics Forum | Wed Aug 21 20:07:51 EDT 2002 | S.Evers
Fritch: http://www.fritschusa.com APS: http://www.apsgold.com MannCorp: http://www.manncorp.com Advanced Techniques: http://www.atco-us.com All of these companies make or sell manual vacuum aided assembly systems which will address your low end asse
Electronics Forum | Wed Jul 09 13:48:03 EDT 2003 | russ
Sam, You may want to be careful with your analisys, reducing paste volume also reduces flux volume. Flux is there to promote and aid in wetting. by reducing flux you may have initiated the poor wetting yourself with the experiment. Just anothe
Electronics Forum | Tue Mar 15 10:34:19 EST 2005 | Patrick
Jimk: My company is a major global manufacturer and supplier of liquid nitrogen. We also provide technical support for electronics applications and aid users in equipping/retrofitting their soldering equipment for nitrogen use. What general state/pr
Electronics Forum | Sun Jul 10 07:17:10 EDT 2005 | Jane Smith
Hi, My name is Jane Smith. I am from Canada. I have graduated a technical college with computer aided design profile. I would like to ask whether somebody knows good places where i can find CAD work online through outsourcing. Thanks a lot
Electronics Forum | Thu Jul 21 16:05:24 EDT 2005 | russ
This is kind of odd, I am accustomed to the Q.C. dept. verifying that criterias/specs have been met per engineering and contractual requirements and not identifying or implementing these specs. I believe that this philosophy aids in eliminating the "