Electronics Forum | Wed Mar 27 21:20:30 EST 2002 | davef
There is two major BGA coating camps. * Camp #1: "We require the coating to be under low stand-off devices but with no filleting. So we apply a thinned dip coat first, and then top-off with a proper spray coat" * Camp #2: "We want no coating under th
Electronics Forum | Fri May 17 15:53:47 EDT 2002 | davef
Based on what you�ve said, comments are: * There is no reason not to expect a trace of Zn in your 85/15 Sn/Pb solderability protection, but Sn/Cu IMC are more prevalent than Zn. * Intermetallic growth and oxidation are very different materials proper
Electronics Forum | Thu May 09 17:28:33 EDT 2002 | davef
There is no IPC specification, nor should there be. * There are just too many peculiarities in the design and fabrication of PWB. * The issue is not defining how to store boards. The issue setting expectation for reliable products and allowing you th
Electronics Forum | Mon May 27 12:14:35 EDT 2002 | arcandspark
I use the exact same paste flux that we use in our solder paste for SMT manufacturing with great success. I have also had great success using the Air Vac DRS Hot Gas units with the same size BGA's. If to much heat is applied to fast to the BGA be it
Electronics Forum | Fri May 31 08:51:09 EDT 2002 | zanolli
Hello Dave, As related to connector mating interface, fretting corrosion is the oxidation of the contact points, causing high resistance across the interface. Fretting corrosion is caused my micromotions in the interface exposing the metalized conta
Electronics Forum | Mon Jun 17 21:16:19 EDT 2002 | davef
You�re correct about J-001. It�s interesting though, I find no references to controlling temperature and humidity as an element of an electrostatic discharge control program in the following: * ANSI/ESD S20-20 * "ESD Program Management" by Ted Dan
Electronics Forum | Wed Jul 17 11:45:48 EDT 2002 | fmonette
The current IPC/JEDEC standard J-STD-033 for moisture-sensitive devices does not include a bake cycle at 90C (it includes cycles at 40C and 125C for non-assembled components in reels or trays). However, the upcoming revision, which should be release
Electronics Forum | Wed Oct 30 10:55:53 EST 2002 | ahobby
I hope you'll take an answer from the sunny UK. I don't usually read these forums but contribute to similar over here, hence the late response. We have an Invicta Sabre 757 machine in our Demo room, running with Zestron SD 300. We give the PumpPrint
Electronics Forum | Wed Aug 07 11:55:31 EDT 2002 | slthomas
Ron, have a look at http://www.fda.gov/cdrh/dsma/cgmphome.html It would be a nightmare, if your plant is not structured to support it. It's a huge pain in the fanny even when you (alledgedly) are. I'm not sure what you're pursuing, but if you're c
Electronics Forum | Tue Aug 13 17:34:44 EDT 2002 | pjc
The Electra is Electrovert's top-of-the-line wave solder machine. Just about the best you could get. Conveyor concerns should focus on the condition of the extruded rails. A machine that new should not have a problem, buy worth a look see. Find out i