Electronics Forum | Fri Oct 06 15:12:17 EDT 2000 | Dave F
Alberto: Consider Dymax 911. It�s wave solderable and passes Cl ion, copper mirror, SIR, and electromigration tests. We have heard good things about Masterbond uV curables, but have not looked at them. 911 doesn�t cure very deep into the little d
Electronics Forum | Sun Oct 01 23:58:55 EDT 2000 | stuartfd
Dear forum types, 1st timer so be good. I have a customer in China using Coates soldermask that in its self is not a problem. The problem is the flux their using, I think,it appears to have a vary high viscosity. The problem they have laid at my door
Electronics Forum | Wed Sep 27 13:45:35 EDT 2000 | Bill Schreiber
Dear Dreamsniper, A big hidden cost in any cleaning system is the cost of diminished production and rework. I assume you are cleaning the adhesive stencils manually since there is no equipment cost in your formula. Manual cleaning of adhesive sten
Electronics Forum | Tue Sep 26 09:42:38 EDT 2000 | Chris May
I have to agree with Wolfgang & Jacko. Two months ago, I decide to run a lead free paste trial. The paste was supplied by company "X", and they stayed on site to witness evaluation. I trialled the paste using EXACTLY THE SAME equipment, stencil and
Electronics Forum | Sat Sep 30 23:57:11 EDT 2000 | DL
I have to agree with Geo. I've a number of years exp. with Quad Machines and currently waiting for the Installation of the APS-1H so I can be trained. However, the quad techs take no prisoners when it comes to chasing down bugs. The Meridian is Quads
Electronics Forum | Mon Sep 11 14:15:28 EDT 2000 | Gary
I am looking for some details about the failure modes in popcorned components. Does the component usually fail to operate. Is the damage likely to extend to the gold bond, wires, or substrate. We have experienced a high failure rate on a subset of
Electronics Forum | Mon Aug 28 17:54:59 EDT 2000 | Steve Thomas
We're trying out 0603 packages on some 0805 footprints (at this stage only on some test boards) since our vendor tells us the 0805's are going to be getting harder to get, and more expensive to pay for. I understand the IPC footprint for the two is
Electronics Forum | Mon Aug 28 15:34:19 EDT 2000 | Steve Harshbarger
Hello Ramon, This is a very common problem that usually can be overcome. Can you tell me the flux type you are using (manufacturer, and flux number)? Has your board vendor, or type of PCB's changed (are they entec coated - bare copper)? What is t
Electronics Forum | Mon Aug 28 14:12:51 EDT 2000 | Earl Moon
1/4 thimble! Obviously, you read none of may articles. HASL has more than a simple topographical problem, and so on. You also would know that TCE, while being an important issue, can be overcome as a problem with optimized pad designs. You would kno
Electronics Forum | Thu Aug 17 01:31:31 EDT 2000 | Dreamsniper
Steve, I'm using 5 Sn/1.5 Ag/93.5 Pb Solder wire with a melting point of 300 deg. C to connect my thermocouples on smd components for thermal profiling. I'm using a soldering iron with an adjustable temp. to be able to melt my solder wire. Temp is ab