Electronics Forum | Tue Dec 04 13:23:05 EST 2001 | fmonette
Hi Steve, It sounds like your product will have many moisture-sensitive devices on both sides. You should be aware of the additional controls that are required to insure the reliability of these components in a double-side reflow application. The
Electronics Forum | Mon Aug 26 20:31:34 EDT 2002 | davef
Yes, it is quite common. Does it [refraction] provide adequate resolution? => Depends on: * What you mean by �adequate�. * When during the process [cleaning solution life] you make the measurement. Is the [refraction] measurement affected signifi
Electronics Forum | Wed Dec 12 07:38:04 EST 2001 | smtspecialist
I have observed the same thing with solder composition in this case I am using 63/37 NC which is giving good results usualy. The liquid tin, product from MG Chemical that I used is to tinplates copper circuit on PC boards. I tried on few relays, it
Electronics Forum | Wed Dec 05 22:38:40 EST 2001 | Ivan R
Hello Chris , Well I have work with MYDATA , QUAD and PANASONIC before and now with SIEMENS that is my background to reply to your question . What I can tell you is that MYDATA is the easier machine to fix any equipment breakdowns and that does
Electronics Forum | Thu Dec 06 11:01:19 EST 2001 | Carol Stirling
This SMT process certainly makes a body want to win the $$$ and retire! We have been trying to stabalize the process and keep running into new problems. Any help would be appreciated on this issue. All pads on both sides have the same look - partial
Electronics Forum | Thu Dec 06 19:46:08 EST 2001 | davef
First, we�re assuming that we�re talking hot air solder leveled [HASL] bare boards, eh? Consider using A-600 - Acceptability of Printed Boards as the basis for discussing the bare board problems. It is the bare board analog of A-610 - Acceptability
Electronics Forum | Fri Dec 07 10:56:24 EST 2001 | franciscoioc
HI, I exeperience this problem before and I tried diferent type of solder pastes.The one that help my process is a Kester solder R596L OA this is a water soluble paste that i am very sure is going to help you.You can get the technical data at http:/
Electronics Forum | Fri Dec 07 13:15:45 EST 2001 | slthomas
We've experienced similar problems with film caps, specifically Panasonic's parts that are alledgedly compatible with both reflow and wave soldering. They are identified with either GB or JB p/n suffixes, which become either GX, GC, or JC for the ref
Electronics Forum | Fri Dec 07 15:23:27 EST 2001 | davef
I'm with Brian. TIN COATED 0603 FAILURES Welcome to the lead-free generation. ;-) The Eurolanders are so blanking stupid, it just makes my head hurt. But then again, it doesn�t take much. OK, enough pontification. Your profile is setup incorrec
Electronics Forum | Mon Dec 10 16:44:51 EST 2001 | davef
Good for you!!! Similar to Steve's comments ... 1. NON-WETTING DEFECT: Yes. Your Lonco is a �stand and deliver� flux. Not some limp wrested impersonation of a flux like most nc fluxes. Without speculating about �incompatability�, recognize that
winsouce.jpg)