Electronics Forum | Fri Nov 06 12:15:19 EST 2015 | derrikf
Also, for anyone who's taken an interest in this thread: We just received samples of Henkel/Loctite's room temperature stable(yes, you read that right), halide-free, lead-free pastes, both the GC 10 and the GC 3W (which is a water soluble/wash paste
Electronics Forum | Thu Feb 24 11:02:29 EST 2000 | mark scheunemann
I am looking to discuss 0402 issues, specifically tombstoning/unsoldered. Any recommendations on pad size/spacing, stencil design etc would be helpful. Placement and reflow profile look good.
Electronics Forum | Fri Oct 06 05:56:37 EDT 2000 | Alberto Silva
Hi, Instead of using High Temp solder, I would like to use a UV epoxy to atach termocouples to reflow profile boards. Does any one know a good one? Thanks in advance. Alberto
Electronics Forum | Thu Feb 24 11:02:29 EST 2000 | mark scheunemann
I am looking to discuss 0402 issues, specifically tombstoning/unsoldered. Any recommendations on pad size/spacing, stencil design etc would be helpful. Placement and reflow profile look good.
Electronics Forum | Tue Apr 17 21:19:31 EDT 2001 | davef
Curious. Tell us more about: * Murata solderability protection * Solderability protection on the caps used to replace the Muratas * Reflow profile used with each of the two pastes * Differences in the two pastes
Electronics Forum | Thu Aug 24 13:21:57 EDT 2000 | Dave F
Please compare indium (In) / Tin (Sn) paste properties in terms of reflow profile, creep, grain structure, etc with other major no-lead solder formulations.
Electronics Forum | Thu Jun 21 16:24:24 EDT 2001 | jdtpfacreate
OEM Boy, Reflow depends on your paste type also. Are you using lead free or will you be going to lead free soon? If your are going to you might want to consider developing two different profiles for lead free and leaded pastes. Good Luck! J.D.
Electronics Forum | Thu Jun 21 16:27:06 EDT 2001 | jdtpfacreate
OEM Boy, Reflow depends on your paste type also. Are you using lead free or will you be going to lead free soon? If your are going to you might want to consider developing two different profiles for lead free and leaded pastes. Good Luck! J.D.
Electronics Forum | Mon Jul 02 20:11:28 EDT 2001 | davef
It's possible that N2 vogued at the dawn of the NC age. Once practitioners jiggered their profiles and more importantly, paste suppliers developed a decent product; the demand for inerts declined. Day-off sound like a fair trade.
Electronics Forum | Mon Jul 23 20:23:19 EDT 2001 | davef
Flux charring * Cool-down too long => Coarse grain ps: Some would argue that potentially you'd get greater response in the process forum rather than the design forum