Electronics Forum | Thu Feb 11 06:50:17 EST 2010 | CL
Good Morning Bryan, We are using Mirtec MV-3 AOI's with 4 megapixle cameras. We use them for 100% post reflow. We are checking, presence, polarity, value, solder, bridging,component height for BGA, QFN etc... and 1st piece validation for machine set
Electronics Forum | Sun Jan 11 11:59:13 EST 1998 | Bob Willis
VP does work well for BGA Technology but it is not any great improvement on convection reflow. It has been stated in a coulpe of articles that there is no delta T difference with VP from the surface ofthe board and under the BGA. That is not true jus
Electronics Forum | Thu Jul 29 00:42:32 EDT 2004 | C.W
hello, BGA was a little excessively reflowed with dwell time(above 183C - solder paste = 63/37) over 2 min, peak temp is 218C. I inspected the BGA under X-ray and there is a little voids but within the acceptable range, i then used the Ersascope to c
Electronics Forum | Tue Jan 16 13:47:24 EST 2001 | cebukid
10% on various BGA packages. I checked the profile and we are getting "ideal" reflow conditions (~ 60 sec. T.A.L.). Ramp rates, temperature deltas before spike zone, and cooling rates are ideal too. I don't believe it's a profile, print, or paste
Electronics Forum | Mon Jul 20 13:52:43 EDT 1998 | John
Does anyone have experience with the Heller 1088 Series ovens?? I am interested in their performance when used to reflow cards sized from 2"*4" up to 8"*12" All reflowed parts would be 0608 up in size and nothing like BGA's or pine pitch will be us
Electronics Forum | Tue May 22 17:21:43 EDT 2001 | davef
BGA require placement accuracy of only 0.3mm (�12 thou), compared with a required placement accuracy of 0.08mm (�3 thou) for fine pitch devices. Even with this level of misalignment, plastic BGA self-center / self-correct during reflow due to symmetr
Electronics Forum | Thu Jul 25 03:01:25 EDT 2002 | martz
We experience e-test failure due to BGA problem. The product was subjected to 40 deg.C hot air blowing on the BGA area and it works pretty well. The product then failed when the temperature became 36 deg. C as the hot air blower is withdrawn. If it
Electronics Forum | Fri Nov 10 17:44:48 EST 2000 | Dave F
In response to your questions: Is the embrittlement from excess gold in lead / tin solder connections bad? It can be vereeee bad. Does it affect all plating processes the same? Give us a break and read the SMTnet Archives, for instance: BGA prob
Electronics Forum | Mon Aug 24 08:34:14 EDT 1998 | JUSTIN MEDERNACH
| Hi, | Does anyone has experiences in reflowing Ceramic BGA and found solder wicking ? Solder wicking has the syndrome that solder being wick from the pad and ended up in the leads. | We have rule out the possibility of not printing any solder paste
Electronics Forum | Thu Mar 01 12:08:33 EST 2007 | rob_thomas
It sounds like something is a little off here. ROHS compatible and ROHS capable parts are going to be ok with a leaded solder paste and processing unless you are building high reliability product.( some are going to argue that even high rel products