Electronics Forum | Tue Feb 19 16:34:15 EST 2002 | djarvis
Dave, Nice one. I was a roadie for Men At Works' tours to the States in '82 & '83. W had a crew t-shirt printed up that had on the front the musical notation for the hook in 'Who Can It Be Now' with the words printed underneath 'Who F.....g Cares'. O
Electronics Forum | Wed Feb 20 02:20:10 EST 2002 | madreindeer
All, Thanks for your answers and (CAaaaaal)yes I would like to have a detailed list please. This is a new field to me as I do have to look after a production in Europa and far east. Most of the times money is not a problem but,They want to know ho
Electronics Forum | Wed Mar 20 13:49:15 EST 2002 | cabjerk
Hi All; The following is from our Support people who worked with Fuji on the problem; Last week Luke Mittur and John Gudel were in from Fuji to address the IP3 issue outlined below. The problem ended up being that the table "up" and table "dow
Electronics Forum | Wed Jun 19 14:44:11 EDT 2002 | kenbliss
It sounds like your inspector improved quality and pre-staging your feeders dramaticaly increased uptime on your machine, thats great to hear. One cautiionary note, be careful not to flood your production area with parts off of your SMT line. With
Electronics Forum | Mon Jul 29 21:45:13 EDT 2002 | davef
Your board fabricator can tell you how they want you to specify boards that do not have solder on the fiducals on the rails. They probably do not need some BIG stinking drawing change, but can operate from a letter. [And even if you run the change
Electronics Forum | Fri Aug 30 00:47:53 EDT 2002 | TLe
Dave, you did not understand my problem right. We don�t get paste on the PCB in the printing phase of process. I have seen also poor wetting on OSP, as you descriped, but that is very unusual. I think generally OSP is better than gold/nickel if spea
Electronics Forum | Sun Sep 15 15:08:00 EDT 2002 | jersbo
My 2 cents... Screen printing may very well have a leg up on deciding SMT defects... however if you pay attention to your stencil (aperture size ratio etc..) and inspect your prints... I believe its a much lesser number... (paste MFG also plays a ro
Electronics Forum | Tue Sep 24 19:07:43 EDT 2002 | davef
Why does the person posting need post to the old tread? What can't the new poster just say [words to the effect] Hey yall!!!! I was perusing the fine SMTnet Archives and came across the following thread: http://www.smtnet.com/Forums/index.cfm?fu
Electronics Forum | Wed Nov 06 14:57:56 EST 2002 | rmorford
Nothing funny seems to happen to the connector when heated. I have no idea how to monitor the temperature of a good pad vs. a bad pad because I have no idea before reflow which ones will be good and which will be bad. I did take a board and rip the
Electronics Forum | Thu Nov 14 10:03:40 EST 2002 | davef
Doug, Ooooooooo. You're correct Vinny has to be talking about Rogers teflon boards. Vinny, There are many different types of PTFE based products. Generally speaking, PTFE has a melting point of 620degF and withstands solder reflow and HASL proce