I was wondering if anyone knows the best way to clean oxides off of fine pitch components? Apparently the paste we use does not have strong enough flux to remove the oxides off of the leads of the components. I have validated the profile and that i
Electronics Forum | Thu Jul 30 14:16:27 EDT 2009 | joeherz
We are running a selective solder machine using SN100C alloy. We have had J-STD-001 analysis performed every 2 months and our last analysis showed our nickel content at 0.104%. The max allowed is 0.100%. We changed out the pot (only 30 lbs) but I'
Electronics Forum | Thu Aug 06 21:50:19 EDT 2009 | fishingfool
Well Orbotech is basically out of business. They have sold their AOI to a company that is a basically a reseller. What that means is usually they have no people to improve software or make changes to improve the system. Not sure how Sony supports th
Electronics Forum | Thu Aug 20 18:20:21 EDT 2009 | joeherz
Sergey, With that many leads and contact surface area points, it doesn't make sense that the part would move as it has without a gust of wind.... What is your confidence that you don't have an MSD issue on this part. Being that it is a TQFP, it's
Electronics Forum | Sat Nov 14 19:27:34 EST 2009 | casmt
I have been programming Mydata for years. Aegis is the most flexible. You can program every field or you can do just the basics and finish it at the machine. I have used Valor but it wants to control everything, it dumps the databases every time you
Electronics Forum | Tue Nov 29 19:48:10 EST 2011 | emrtech
I have created an excel macro that will work with my100 and my9. this macro (excel spreadsheet will work with excel 97 through 2007) will generate the PCB .gen file to import into my9 or my100. the components can also be imported before generating th
Electronics Forum | Sat Sep 05 02:34:19 EDT 2009 | martinphill
check R-axis mechanical backlash... After checking R Axis Backlash, Coupling. If still the Problem continues. We have the same issues & when we asked Jagadeesh Rajagopalan , he suggested following action item Check the servo Error display. If it i
Electronics Forum | Wed Aug 26 10:48:30 EDT 2009 | grahamcooper22
Some print expiry date on reels and some specify a shelf life on data sheets. Two main reasons are that the flux in the wire is a mix of chemicals and over time in storage these can react so soldering performance can be changed. Although I have to sa
Electronics Forum | Tue Sep 08 16:18:20 EDT 2009 | proy
We have an Orion which has been running very well. We just started to run production of a board with NO changes from the last run about one month ago. Today, however, the vision system is not recognizing parts. The scan image on the monitor looks goo
Electronics Forum | Thu Oct 01 16:56:40 EDT 2009 | gplume
Does anyone out there have experience soldering with Pb solder (Sn 63 or Sn 62) to SAC 305 coated PCB lands (about 50um) or Sn-Cu plated lands (about 10um). I know soldering Pb free (Sac based soler) to Pb/Sn coated lands is a no-no, but was waonderi