You have a rather old machine that you are running....now realizing this you need to check some things. 1. Clean the scales in the x and y direction. On some of the encoders there is an led to see if its reading correctly....Usually it turns green b
Electronics Forum | Fri Jul 18 15:25:19 EDT 2014 | davef
The presence of agitation at an air / solution interface and a foaming agent causes foaming. Most water soluble fluxes contain surficants. Surficants are foaming agents. First, it's likely this foaming is caused by poor control of the temperature of
Electronics Forum | Fri Jul 25 10:11:36 EDT 2014 | cgreiner
We also had this problem and found similar results with the anti-backlash nuts binding. We went through the process of cleaning the lead screws and the nuts which resolved the problem for about 6 months only to have it return. We learned that the
Electronics Forum | Fri Jul 25 10:13:01 EDT 2014 | cgreiner
We also had this problem and found similar results with the anti-backlash nuts binding. We went through the process of cleaning the lead screws and the nuts which resolved the problem for about 6 months only to have it return. We learned that the
Electronics Forum | Mon Sep 15 14:14:47 EDT 2014 | riot983
Hi guys, New to the forum. I always read and look around at used equipment but have never posted. Anyway, I operate a Mydata My9 at a small shop and have recently ran into a problem and wanted to get some good advice. An employee of mine cleaned the
Electronics Forum | Thu Jan 29 09:18:36 EST 2015 | davef
Nichrome, manganin, phosphor bronze etc are easy to solder ... the hard part is removing the corrosion * Manganin: 86% copper, 12% manganese, 2% nickel. Often, it's used in making cryogenic measurements, due to its low heat loss. * Select a flux for
Electronics Forum | Mon Feb 09 09:00:17 EST 2015 | jax
Outside the MSD issues stated already (and I cannot provide a exact time not knowing multiple factors like Humidity levels, temps, exposure times, etc...) OSP might be the very worst finish to use in this scenario of side 1 / store on a shelf / side
Electronics Forum | Wed Feb 25 21:47:24 EST 2015 | dinhhuunam
Hi Marshall Bartel, SJ INNOTECH Printer is Best solution & Service for you ! HP-520S/HP-620S/HP-760S/HP-1000S Printing (±0.0125mm) Repeatability (±0.01mm) 0.3 Pitch QFP, 0402 Chip, Ø0.2 MBGA Speed/pressure control by printing section (5 sections) V
Electronics Forum | Wed Feb 11 08:33:25 EST 2015 | daniel_esposito
Hi, I have two Quad IVc and both of them have the same problem. Laser Alignment is not working! When I run funtion 30, it always gives 1 at nozzle height. If I place any object beside the nozzle, it will give a number different from one depend on how
Electronics Forum | Thu Feb 12 12:30:16 EST 2015 | stevezeva
I remembered something from the TechNet a long time ago about heating the board with a heat gun to see if the white spots disappear. I searched the archives and found this from Bill Kenyon: Quick identification of solder mask white spots- if it is t