Electronics Forum: conveyor technologies wave incline conveyor (Page 1 of 3)

wave soldering and solder bridge

Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc

5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht

Wave Soldering - Icicling/Bridges

Electronics Forum | Fri Jan 24 17:05:37 EST 2003 | pjc

Correction: The Ultrapak (UPK) 600 and Electra models allow for conveyor incline adjustablity from 4 to 7 deg.

Wave Soldering SMT IC

Electronics Forum | Mon Oct 16 11:10:51 EDT 2000 | PeteC

Excessive bridging on SOICW-20, -16, SOIC-8, -14,-16. I've got a board, 4" x 6" w/ SOICs on bottom-side for wave solder. I've checked topside board temp for flux activation, wave height, wave surface with the glass check-plate going from 1" to 2" spa

bulbous joint

Electronics Forum | Thu Feb 19 18:07:57 EST 2004 | davef

We're inclined to buy Russ's stuff about peel from the wave. Look here, but shield your eyes first: [ http://www.thepdfshop.co.uk/ppm/defects/Wave/asp/50.asp ] [A respectful bow to BW for the pix] Could you tell us more about: * Board direction thro

Wave information

Electronics Forum | Mon Dec 12 22:14:42 EST 2005 | davef

�a va Frank? Well, popularity depends on the beholder. Never heard of your "Specnor" machine. US and Eurolanders take different approaches to conveying boards. * US: Finger conveyors * Eurolanders: Pallet conveyors Suppliers of wave solder machin

3355-11 Uh oh!

Electronics Forum | Wed Jun 24 13:46:41 EDT 1998 | Chris Kelly

Brian, a couple of things really stick out here... 1) You are spraying what is referred to here at the CATT as "PINK DEATH" The 3355-11 is about the most active/aggressive flux you can get your hands on. I am concerned about both the condition

Wave Solder Profiling Basics

Electronics Forum | Fri Jun 25 09:51:35 EDT 1999 | C.K.

| Dear John/Earl | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired profilin

Re: Wave Solder Profiling Basics

Electronics Forum | Fri Jun 25 12:01:49 EDT 1999 | Earl Moon

| | Dear John/Earl | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired

Re: Wave Solder Profiling Basics

Electronics Forum | Fri Jun 25 16:54:25 EDT 1999 | C.K.

| | | Dear John/Earl | | | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the

'Blue solder' residues

Electronics Forum | Thu Oct 28 11:41:21 EDT 2004 | Steve Stach

Hello Loz, Blue residues on circuit boards can be caused by copper corrosion, component body deterioration, marking permanently, and adhesive break down. In this case, a more subtle mechanism appears to be possible. This is a no clean application

  1 2 3 Next

conveyor technologies wave incline conveyor searches for Companies, Equipment, Machines, Suppliers & Information

Selective Soldering Nozzles

High Throughput Reflow Oven
Best SMT Reflow Oven

World's Best Reflow Oven Customizable for Unique Applications
Electronics Equipment Consignment

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...
IPC Training & Certification - Blackfox