Electronics Forum | Fri Jun 04 03:03:52 EDT 1999 | Scott B
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Fri Jun 04 15:04:16 EDT 1999 | Earl Moon
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Mon May 25 23:26:19 EDT 1998 | Jon Gruett
I agree with Mike. They are a dead issue. As a manufacutrer's rep for many types of equipment and 11 years in the engineering field I have seen several attempts to revive the technology (if you can call that technology). Most if not all attemptds
Electronics Forum | Fri Jun 04 10:02:06 EDT 1999 | Chrys Shea
| | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole
Electronics Forum | Fri Jun 04 17:10:59 EDT 1999 | C.K.
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Tue Jun 08 11:40:03 EDT 1999 | Steve Skinner
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Thu Aug 20 18:11:53 EDT 2009 | smt_guy
Hi davef, thanks again for that enlightenment. I'm just curious about what's happening with the solder joint of the said process. Again to add to my unending queries for now: So on top of that copper is a thin layer of lead-free solder composition
Electronics Forum | Thu Jun 17 10:22:51 EDT 2010 | floydf
Last July I posted a query about reflowing leaded paste to gold plated boards, I wasn't getting a good reflow. The answer that seemed to work was dwelling the board at reflow for the maximum recommended amount of time. Would anyone have an opinion on
Electronics Forum | Wed Dec 05 17:30:02 EST 2001 | davef
How do you know that "approx 450�C" is "too high"? As a side, the temperature on the temperature sensor is: * Inaccurate. * Not the temperature at the solder. Listen, operators are smart people. They have figured-out that they can solder faster wi
Electronics Forum | Thu Apr 17 05:14:40 EDT 2008 | gregoryyork
I have seen similar things like this before with Solder Resist redepositig back on the pads, this is a clear residue very hard to see. Solder resist will obviously resist solder adhering to it. If you rework the boards then the heat of the iron will