Electronics Forum | Mon Dec 17 12:12:18 EST 2007 | Claude_Couture
in very rare occasion I had problems with BTU ovens, I contacted BTU directly and they were always helpful.
Electronics Forum | Thu Dec 13 09:58:54 EST 2007 | cokedigits
I am a startup and would like to invest in training materials. Are these materials from the IPC any good? http://search.ebay.com/search/search.dll?from=R40&_trksid=m37&satitle=ipc+training&category0=
Electronics Forum | Mon Dec 17 10:12:53 EST 2007 | fastek
If you have worked with Panasonic chipshooters in the past then you have all the experience necessary to make a wise decision.
Electronics Forum | Tue Dec 18 21:05:26 EST 2007 | ludee_circuits
What kind of ceramic PCBs you need? Please offer more details. We could make PCB using RO4003 and 4350B materials.If there is anything I could do for you,please send me a email : kobe@ludeecircuits.com
Electronics Forum | Thu Dec 13 13:56:24 EST 2007 | greg_diaz
I would like to know if anyone out there is using a stand alone Board labeling equipment and what type.
Electronics Forum | Thu Dec 13 15:35:14 EST 2007 | mulder0990
Our plant does not use an automated process, but I have done some research to the LPF Label Feeder by hover davis. It is for the Fuji IP, QP2, QP3, XP. Hope that will point you in some direction or get this thread started.
Electronics Forum | Fri Dec 14 10:08:17 EST 2007 | lconnor
We used to use in line labelling machines. They are currently for sale. http://www.equipmatching.com/used_equipment/2/34/89063.php
Electronics Forum | Fri Dec 14 10:13:46 EST 2007 | Frank
Hover Davis has two models of their label feeders. 1) Pre-printed labels 2) Print on demand.
Electronics Forum | Thu Dec 13 14:49:07 EST 2007 | 26560
Any recommendations/data on a superior flux to use for Package on Package assembly? Also, any guidelines on flux depth, viscosity, etc... are welcome.
Electronics Forum | Thu Dec 13 17:12:38 EST 2007 | jseagle
Has anyone heard of this? I was told that this would help SN100 in the wave solder by making it flow better at a lower temperature? Thanks James