Electronics Forum | Fri Nov 18 07:09:41 EST 2005 | avalancher
What Bruce is referring to is a TPSys Data server. You can give it any name that you like (in Bruce's case, it must be called MyServ). I think what he is asking is after the reboot, does it have trouble reconnecting to the 'master' (whether that be a
Electronics Forum | Wed Nov 09 08:33:32 EST 2005 | gregp
Sounds like the vision is having trouble deciphering what is the component and what is the background. The problem is what if the plating is inconsistent (sounds like it is)? In this case with front (reflective) lighting the problem may never be so
Electronics Forum | Wed Nov 09 07:55:10 EST 2005 | pavel_murtishev
Good day, Is there on the market any machine independent barcode reading system? We have some placement machines with build-in barcode reading system. When operator changes the reel with components he/she checks reel with barcode scanner. Some of th
Electronics Forum | Thu Nov 10 08:23:35 EST 2005 | arclightzero
Hello, I am currently trying to isolate internal fallout problems with very low yield substrates mixed with great yields and have recently found that we are using a Sn62/Pb36/Ag2 solder paste with full tin (no lead) components as well as Pb95/Sn5 sol
Electronics Forum | Thu Nov 10 10:03:02 EST 2005 | R.Powers
Hello, I am a high volume user of bulk component feeding. We are going to be changing some of our feeding interfaces and I need to find suppliers of SMD cassettes. I need someone who supplies just the plastic cassette, not components in a cassette
Electronics Forum | Thu Nov 10 21:15:39 EST 2005 | davef
Years ago, there was discussion of making a "IPC-A-640" to define requirements for assemblies comprised of more than a circuit board assembly. We don't know what happened after that. As an alternative consider: Telcordia GR-78 - Generic Requiremen
Electronics Forum | Fri Nov 11 04:40:18 EST 2005 | pavel_murtishev
Good day, First of all used solder paste should be placed in special container. It should be kept separately from �fresh� solder paste from the same jar. Limit paste usage period after opening the jar according to manufacturer�s specification. When
Electronics Forum | Fri Nov 11 10:32:12 EST 2005 | davef
Rob: After SAB purchased Pilsner Urquell, they changed from using hops to a extract of hops in their process. They changed the foil on the neck of the bottle from silver to gold at the same time. The result was PU went from THE UNDISPUTED BEST bee
Electronics Forum | Fri Nov 11 06:58:03 EST 2005 | bk
A little more information on your current wavesoldering process would be helpful in helping you. Information like what kind of flux your are using,how you are applying the flux,what preheat temps you are using,and your conveyor speed. Without knowing
Electronics Forum | Fri Nov 11 08:30:12 EST 2005 | GS
HI all, which is the last "though" about the max Pb % allowed/acceptable into a Pb Free Alloy ? For istance inside : - HASL Process Solder Pot Alloy - Wave Solder Pot Alloy ( 400Kg mass average) - Static Wave Solder Pot Alloy - Etc IPC-J-