Dear Dave and Mike, I do not normally respond to threads of the forum. However, I do enjoy reading other's comments. There is a lot of valuable information provided by both suppliers and users. You seem to be making light of Bill Schreiber's com
Electronics Forum | Tue Mar 13 14:25:14 EST 2001 | Mike Konrad
Hi Kerry, I do not wish to turn this subject in to a debate, but consider this� If every technical question posted resulted in a commercial reply (company name, model number, phone number, price, features and benefits, etc), then there would be lit
Electronics Forum | Fri Mar 16 07:46:56 EST 2001 | C. Robert Nelms
David Thanks for telling me about this web-site! Great site! I very much appreciated this message. To be honest, after reading some of the other messages here on this forum, I almost decided that this site was not for me. Seems like most / all o
Electronics Forum | Mon Mar 19 21:25:13 EST 2001 | davef
The technique you describe is contrary to the approach we've taken to educating our folk and helping all to understand what's going on and being involved. Not sure how well that would play in Peroria. I'm looking for tools / techniques / what not t
Electronics Forum | Tue Apr 17 08:29:12 EDT 2001 | Geertjan de Beijer
My name is Geertjan de Beijer and I am new on this forum. I have a question about Electroless Nickel/Gold finishes. Until now we always use a HAL finish on our PCB's. Since we are using compontents with pitches of 0.5mm we notice that the HAL finis
Electronics Forum | Tue Apr 17 10:17:10 EDT 2001 | genny
Hi, ENIG finish is the same reason I came to this forum for the first time a few months ago. I found a bunch of useful information by searching the archives. Check it out. ENIG has some good properties like flatness, and the process control has i
Electronics Forum | Tue May 15 15:15:53 EDT 2001 | ohboy
Hi all, I just discovered this forum and I'm very impressed. We have a vendor who recently stopped placing desiccants in the vacuum packaging for our pcbs. (Yes, it's on the dwg!) His reasoning was that the desiccants can degrade the finish on the
Electronics Forum | Fri May 25 17:25:25 EDT 2001 | morefun
Is anyone out there is the contract or the OEM sections using viscometers to check solder paste or glue for acurate process definitions. By this I mean check the materials viscosity over a period of time and measure the degradation of performance, t
Electronics Forum | Thu Jun 14 21:23:36 EDT 2001 | davef
Oooo, big bucks wusher!!! Consider the SMTnet Archives a valued resource. For instance, look at: http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=1632&mc=2 As far as your resistivity measurement is concerned, you hav
Electronics Forum | Mon Jun 25 20:54:28 EDT 2001 | davef
No, I�m suggesting an increase in the distance between the two pads on the board. This "G" in SM-782A "Surface Mount design & Land Pattern Standard" parlance. You shouldn�t fight solder balls for long periods. You should just increase the pressure