Electronics Forum | Fri Sep 14 17:41:04 EDT 2001 | bdoyle
SMTnet will be down Saturday September 15th from 9AM EST until no later than 5PM EST for scheduled maintenance. We appologize for an inconvenience this may cause.
Electronics Forum | Mon Sep 17 09:44:29 EDT 2001 | gresko
Dave, Ceramic sheets of that size are not always flat and as a result will sometimes crack when clamped along the full edge. Point clamping will hold the substrate secure for placement. If you are not processing in a pallet make sure that you have
Electronics Forum | Mon Sep 17 17:49:02 EDT 2001 | arzu
What about the material of the stencil? Nickel formed? stainless steel? even more materials are available, some with different ways to form the apetertures.
Electronics Forum | Wed Sep 19 10:19:28 EDT 2001 | davidd
Hi Jake, in your experience, what to do feel is the level of automated 3D paste height or volumetric inspection required moving to the 0201 process control requirements and defect detection. Dave
Electronics Forum | Sat Feb 09 17:33:30 EST 2002 | George Verboven
For more info about Metal Stencil Overview. also look at: http://www.tkb-4u.com/articles/printing/metalstenciloverview/metalstenciloverview.php
Electronics Forum | Mon Sep 17 10:09:45 EDT 2001 | martys
What variables that you have tested are sensitive to producing tombstoning defects and what advice can you provide to minimize them?
Electronics Forum | Mon Sep 17 10:11:26 EDT 2001 | jstarkweather
What is the tightest spacing that you have assembled 0201 components? Under what assembly scenarios did you produce the best/worst yield at this spacing?
Electronics Forum | Mon Sep 17 10:29:01 EDT 2001 | ksfacinelli
Please describe what was found to be optimal print parameters. I am also interested in hearing about stencil and design layout considerations. Thanks, Kevin
Electronics Forum | Thu Sep 20 15:12:47 EDT 2001 | ert002
No problem on the feedback. Should I just reply to the same thread or email you directly at DEK? This is my first time using this site, but I imagine they have the capability to attach files, pictures, etc. I will probably be completing the study
Electronics Forum | Mon Sep 17 16:12:37 EDT 2001 | gswable
HI EVRYONE I AM A REASEARCH STUDENT AND AM COMPILING A REVEIW OF TECHNOLOGY ROADMAPS OF VARIOUS EMS PROVIDERS SO THAT WE CAN COMBINE TOGHETHER AND LOOK AT WHERE OUR EMS INDUSTRY IS HEADING . SO IF ANYONE CAN HELP ME WITH LINKS FOR SUCH ROADMAPS