Electronics Forum | Tue Aug 03 03:13:17 EDT 2004 | V.R.Kini
Bent nozzle can result in vaccum leakage resulting in parts falling during part pick up. Correct this. However, if your machine has laser/vision alignment, you should not be having a problem since these come in to picture after pick up. If you have a
Electronics Forum | Tue Aug 17 13:24:47 EDT 2004 | blnorman
We have parts that have electroplated tin over nickel. The mfg. assures us the minimum thickness of the tin is 5 microns. Cross sections have shown many instances of 1 micron and pits that go down to the nickel barrier layer. A request for thicker
Electronics Forum | Wed Sep 08 02:31:17 EDT 2004 | Darby
Check any inventory you have of 0805 3p9 capacitors manufactured by Exxxx in Europe. Batch # 1878029. Mixed values of 3p9 and 220pf are possibly on the one reel. I have never come across this before but we have found 5 reels where this is definite af
Electronics Forum | Sun Sep 12 21:31:49 EDT 2004 | Jim
MAke a new stencile and have the aperatures reduced by 20% in X and Y. This has solved 90% of all solder balling issues I have ever dealt with. Be careful with your fine pitch and micro-BGA's. If you are not having problems with fine pitch and 1:1
Electronics Forum | Tue Sep 21 12:04:02 EDT 2004 | russ
I would lose focus on European machines. I have used several european placement machines and frankly I think that they are garbage. The machines have been poorly designed for Preventative maintenance, replacement parts are expensive and slow to get,
Electronics Forum | Mon Nov 29 13:01:35 EST 2004 | bobsavenger
I have a DEK 265LT screen printer and a Fuji bare board loader. I cannot get the two machines to talk through the SMEMA cable. I have the personality card for the DEK and I have the correct cable for a FUJI machine. Is there something that I nee
Electronics Forum | Tue Jan 11 03:43:51 EST 2005 | Scott B
We have had similar problems and have abandoned use of MySpeed. I don't know what version of Mydata software you are running but have started to use the 'Hydra Preparation' function within TpSys 2.3 to arrive at optimised set-ups. Mydata advise that
Electronics Forum | Thu Jan 13 09:08:52 EST 2005 | rlackey
Good point, but there are not many companies that actually have built machines that have worked robustly & reliably for 20 years. That is a little unfair to newer entrants to the market, but then again reputations are earnt. Regarding flexible ma
Electronics Forum | Tue Feb 01 11:33:26 EST 2005 | Indy
Hi Jay, please let us know your inputs from the seminar regarding SN100 Nihon solder from FCT. This solder seems to have a higher melting temp of 221C. It prints well and visually looks similar to SAC alloy. Have no reliabilty data though. Jay
Electronics Forum | Tue Jan 25 13:28:51 EST 2005 | Ron Stubblefield
HELP!! I need an exploded view of the early-style (AP-20 and some 24's) camera cube. I have bought a used AP-36 and am having vision problems. I also need the cube alignment procedures if anyone has them. I already have a "C" tool. Thanks Ron ro