Electronics Forum | Tue May 05 16:58:08 EDT 2009 | billmeye
I don't have CircuitCam, I'm using Unicam with Mydata. In Unicam I have a Theta Offset setting for each package witch determines the default rotational angle with respect to the pin 1 setting within the package data. With Mydata, the package inform
Electronics Forum | Wed Apr 15 12:57:37 EDT 2009 | bk
I'm not sure if you fixed your problem yet or not but i'll give you some insight on your problem. The x wagon motor doesn't move cause of the voltage it actually moves when there's current applied to it. The voltage dictates the direction the motor m
Electronics Forum | Mon Apr 13 14:36:18 EDT 2009 | leemeyer
I have seen this problem before. There is a cable that runs from the Quadalign board to the backside of the backplane. It is not secured in any way so it may have come loose in shipping. Open the right side panel on the machine. The Quadalign board
Electronics Forum | Tue Jun 09 23:00:53 EDT 2009 | davef
Suppliers are: * Asymtek; 2762 Loker Ave West, Carlsbad, CA 92010; 800-279-6835 760-431-1919 F760-431-2678 asymtek.com * Ultrasonic Systems; 135 Ward Hill Ave, Haverhill, MA 01835; 978-521-0095 F978-521-7023 ultraspray.com sales@ultraspray.com Stepha
Electronics Forum | Mon Jul 13 06:30:59 EDT 2009 | hcarrasco
1.- Check your vacuum a.- Check filters b.- Check air flow (the vacuum is generated by a Ventury using air flow, not air pressure) c.- Vaccum vias (Possible linth inside the vacuum lines) 2.- Check the nozzle condition (Probably broken o
Electronics Forum | Fri Aug 21 00:27:09 EDT 2009 | boardhouse
Hi To Start Min Tg is just a portion of picking a lead free material, the other is Td. We recommend the following to our Customers. 2-8 layer 150 Tg. Min. / 340 Td. 8-Up. 170-180 Tg.Min. / 340 Td. The above recommendations have been used by man
Electronics Forum | Sun Aug 23 07:03:09 EDT 2009 | ghepo
OK Eric, is difficult answer at distance without examine the PCB..., anyway in my opinion the problem is the PCB quality. There are two possibility : the crack is between solder and nickel or is between nickel and pad copper. In both situation the
Electronics Forum | Tue Sep 08 20:32:55 EDT 2009 | juanv
Hi, This is the firstime that I'm working with a HP 3070 Series 3 ICT. We ran the first assemblies and I would like to know where could I find all the information about this first article run. Fist of all, I need to know how could I visualize at
Electronics Forum | Fri Sep 18 00:39:23 EDT 2009 | rohitfast
Hi Davef & Mikes, Thanks for the response. I am agree with both of your point. If the component bosy will be fall in Coductive or dissipative range, there are chances of shorting. Other thing in ESDS:2020 8.3 para is saying to keep away all the insul
Electronics Forum | Thu Oct 01 07:09:53 EDT 2009 | g2garyg2
Good Morning Here are a few thoughts. When mfg large flex circuits you will need to fixture them to create a stable production environment. As such, the foot print fo the product grows. So you may require systems that can handle 20 inch width by 38 i