Electronics Forum | Thu May 13 21:45:14 EDT 1999 | ardis
I am seeing reflow around my signal pins after being subjected to a profile of 204c for 1 minute and 225c for a min of 30 seconds. Signal pins are soldered into a copper plated alum. case with SB5 and then silver plated. The pins have a hot oil tin
Electronics Forum | Fri May 14 00:28:09 EDT 1999 | Mike D.
| I am seeing reflow around my signal pins after being subjected | to a profile of 204c for 1 minute and 225c for a min of 30 seconds. Signal pins are soldered into a copper plated alum. case with SB5 and then silver plated. The pins have a hot oil
Electronics Forum | Wed Sep 11 16:57:04 EDT 2002 | bigwop
I've seen this problem caused by the cool down. > On a 7 zone oven I made a profile to peak at zone > 5 to give some semblance of control to the cool > down. The component can develope a big delta T, > because of the difference of materials Che
Electronics Forum | Wed Sep 11 13:20:37 EDT 2002 | stepheno
I've seen this problem caused by the cool down. On a 7 zone oven I made a profile to peak at zone 5 to give some semblance of control to the cool down. The component can develope a big delta T, because of the difference of materials
Electronics Forum | Wed Sep 11 23:20:44 EDT 2002 | scottefiske
Profiles are absolutely the first course of action to validate. A few additional questions would be: * Moisture can cause warping as well, verify the manufacturers recommended handling procedures were followed. * Where is the suspect BGA located
Electronics Forum | Mon Oct 03 10:20:43 EDT 2005 | davef
Follow your component supplier recommendations. For instance: Xilinx says their lead-free alloy for their BGA spheres is SnAgCu, and liquidous is 217*C and they want you to peak at 230 - 235*C for good wetting according to their reflow guidelines.
Electronics Forum | Thu Sep 12 09:15:29 EDT 2002 | mhoughton
I have printed and placed similar devices in high volume with exactly this spec for a couple of years with no problems, are you using laser cut stencils and what type of solder paste are you using? and what is the end use of the product as it may nee
Electronics Forum | Thu Sep 12 10:45:29 EDT 2002 | pbarton
We have used a laser cut stencil 0.15mm (0.006") thick with 0.3mm (0.012") square apertures radiused in the corners 0.06mm (0.0025") to aid paste release. This approach with the (type 3) paste we use has proven successful on thousands of devices plac
Electronics Forum | Fri Mar 28 22:01:00 EST 2003 | MA/NY DDave
Hi Yes I agree, yet this subject is about Tombstoning and oven profile or even oven working correctly across the entire product is a sub-set of how one gets those little chip babies to sit and stay where they belong. Flat and Heeling like their mast
Electronics Forum | Fri Apr 09 12:46:10 EDT 1999 | Bob Barr
I have been using an Air-Vac DRS-22 for almost two years with very good results. Once a profile is developed it is very repeatable. The DRS-22 is no longer available, however. It has been replaced by the DRS-24. Unfortunately, the DRS-24 has a lo