Electronics Forum | Mon Mar 06 11:13:08 EST 2006 | fredericksr
I ran this same process by MyData when I was there for training and I received the message that calibrating the force sensor through the service menu was an invalid technique. Correct me if I am wrong, but every tool should recalibrate itself when i
Electronics Forum | Mon Dec 27 16:55:52 EST 2004 | jdengler
HOSS, Most spray fluxers won't help. If you get a spray fluxer that uses a high velocity spray gun, it might. That being said I had less problems with top side wetting from a foam fluxer myself. Make sure the foam height is good. Also had some pr
Electronics Forum | Tue Dec 28 09:21:22 EST 2004 | pjc
In almost every application an ultrasonic spray fluxer will out perform foam fluxing. Better soldering results are what most expereince after making the change to U/S spray. There are good ultrasonic units from USI and Sono-Tek. www.ultraspray.com w
Electronics Forum | Wed Dec 29 12:33:31 EST 2004 | mmjm_1099
I am writing this to see how many out there use theses programs. I wanted to start a thread for issues or comments for other users or new users to use. I just like to hear new things that a person came across using the program or issues that we can h
Electronics Forum | Wed Dec 29 16:27:24 EST 2004 | Demar
Well I recently went with Circuitcam but I use the MCS platform still. To be honest I am not 100% sold on the software yet. I have already found bugs in the software that will likely never be fixed based on my outdated MCS platform. The only problem
Electronics Forum | Wed Dec 29 17:58:30 EST 2004 | carterhoward
Hi All, We�re a C-M and have been using C-Cam for about 4 or 5 years now. We we�re one of the first customers on there 16 bit platform, so we�ve seen a lot of changes. Our company runs Philips with PPS, and C-Cam has been a rock sold platform. As f
Electronics Forum | Sat Jan 01 10:14:30 EST 2005 | davef
East coast, solder connection failure analysis labs in the vacinity of New England are: * American Competitiveness Institute, Electronics Manufacturing Productivity Facility, One International Plaza - Suite 150, Philadelphia, PA 19113(610) 362-1200 F
Electronics Forum | Mon Jan 03 16:34:10 EST 2005 | davef
The main advantage if ENIG over HASL is that ENIG is flat and HASL generally is not. The main disadvanages to ENIG over HASL are: * Cost of ENIG is 1.5 - 2X higher than HASL * Selflife is less than HASL * You solder to nickel, rather than copper * E
Electronics Forum | Tue Jan 04 15:28:22 EST 2005 | davef
Look here: * Circuit Board Repair and Rework Guide [ http://www.circuittechctr.com/guides/guides.shtml ] * 7711/21A - Rework and Repair Guide [ http://webvision.ipc.org/scripts/mgrqispi.dll?APPNAME=IPCWEB&PRGNAME=TOCFRAME&ARGUMENTS=-N,-N,-A,-A,-N50 ]
Electronics Forum | Wed Jan 05 05:12:04 EST 2005 | sasha
We wand to start using of water-washing-off pastes and fluxes. In the technology of cleaning supersonic cleaning + deionized water at finish will be applied. Hence there are some questions: 1. Is it enough to use only water while cleaning or i