Electronics Forum | Fri Jul 02 10:30:35 EDT 2010 | kevslatvin
We used to use an APS Gold GF-120 before we went lead-free and the HT version came out. It worked fine for low volume and proto runs though not as much control over the profile as an oven with more zones. We actually had a batch oven from Bomir befor
Electronics Forum | Thu Feb 17 09:35:16 EST 2011 | ravo
Hi everybody, I am here seeking your experience and asking your help, I want to update our SMT production line as I already hace FUJI CP6 and QP242 machines beside GL2 and oven our new product including 60 components 0402 (1mm*0.5mm ) and 2 BGAs w
Electronics Forum | Sat Feb 19 11:40:40 EST 2011 | ravo
Hi everybody, I am here seeking your experience and asking your help, I want to update our SMT production line as I already hace FUJI CP6 and QP242 machines beside GL2 and oven our new product including 60 components 0402 (1mm*0.5mm ) and 2 BGAs w
Electronics Forum | Wed Sep 21 17:53:19 EDT 2011 | action_101
I would like some input on reworking BGA's and the best method. I have reworked BGA's since 1998 using both micro stencils and just flux dipping the parts. I have reworked SN/PB and lead-free (AIM NC258) BGA's for the last 8 yrs. with just flux. I ha
Electronics Forum | Mon Jul 25 09:11:25 EDT 2016 | spoiltforchoice
There 2 main rival standards for orientation in tape and because you can't really trust manufacturers to stick to one or the other or something else entirely it is always wise to check the datasheet. Typically an SOIC will have pin 1 the same end as
Electronics Forum | Thu Sep 13 15:09:07 EDT 2018 | reckless
So it took me a few months to figure out the compact reflow oven market. I bought the following ovens: Heller 1500EXL Essemtec RO300FC-C - QTY 2 DDM Novastar Gold Flow - Desktop DDM Novastar 1800HT - Conveyor Zevatech 5 zone oven T962C benchtop ove
Electronics Forum | Mon Dec 30 12:55:37 EST 2019 | emeto
We saw your profile, which in my opinion looks alright based on the guideline from the vendor. Can you tell us more about the joints that you cleaned? Are they showing nice wetting and nice and shiny finish? How about your stencil thickness? From my
Electronics Forum | Tue Feb 09 18:53:20 EST 2021 | SMTA-64387083
You'll have to do at least 2up array since most conveyors won't handle boards less than 2in wide. I'm assuming it's FR4 lead free temperature material and PCB's are scored in the panel. The 13-16in lengths aren't a problem other than depaneling. With
Electronics Forum | Mon Jun 27 20:32:46 EDT 2022 | kumarb
Absolutely..there are many suppliers of this common widget. Here are some names - we use (have met each in HK / Taipei): The 800-lb gorilla / leader of this industry: http://www.kangyang.com.tw But we found Judy (Yazhoulong) to offer the best p
Electronics Forum | Wed Aug 09 12:11:44 EDT 2023 | thecolonel97
We are currently experiencing an issue with one of our reflow ovens producing large amounts of flux crystals in the end of zone 12 and entrance of cooling zone. This has been going on for roughly around 4 years now, we are using Senju M705 lead free