From the picture, I cannot see clearly solder ball violate electrical clearance or cause a short, maybe it is. What I can see is the solder paste has some misalignment although it doesn't printed in solder mask area, but actual position will reduce
Electronics Forum | Sat Aug 05 12:12:05 EDT 2000 | Ramon I Garcia C
Hello Friends: I'm new in SMT process, I have a problem with little balls of solder beside of the component, I'm tried reducing the apertures in the stencil and making home base, some times the balls desappear, but some time not, and some times
Electronics Forum | Fri Sep 02 08:16:14 EDT 2005 | pjc
From Ray P. Prasad's article in this month's SMT magazine about the new IPC-7095 revison: ".....IPC does not have pull tests in any of its standards, and some reliability experts would prefer to keep it that way, pull tests are commonly used by some
Electronics Forum | Fri Feb 23 09:35:36 EST 2024 | emanuel
We have the standard profile as a template made according to the solder paste specs. For some boards we measure the result at 2 points, on the board itself and on top of a sensitive SOT263 module and adjust accordingly. The solder paste is well kept,
Electronics Forum | Thu Jan 27 14:49:53 EST 2000 | Glenn Robertson
Tuan - One of the reasons I suggested pre-tinning (aside from the negative effects of Gold on appearance and reliability) is the known slower wetting of Sn/Ag and Sn/Cu alloys as compared to Sn/Pb. If you don't have to be Lead-free, the high Lead
Electronics Forum | Tue Apr 12 08:25:43 EDT 2005 | davef
Q1 Can anyone explain to me what is the clean and non clean solder? A1 The trend away from CFCs has lead many users to evaluate switching to no-clean soldering processes. The term "no-clean" is actually a common misnomer when used to describe a flux
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Tue Sep 06 10:20:33 EDT 2005 | slthomas
I love these stories. At my previous employer we experienced intermittent failures on an audio microprocessor assembly being used on a *new* product. This board had numerous microprocessors and complex firmware aboard. They discovered one PLCC on
Electronics Forum | Mon Jul 01 20:42:54 EDT 2002 | davef
Comments [questions] are: * It�s strange that an uggie ol� SOIC, 50 pitch, BIG honkin� solder pad, kinda thang is failing. Sumpin aint kosher, yano? * Where is the failure occurring [ie, lead to pad, pad to board, etc]? Talk about the breadth and di
Electronics Forum | Thu Jan 02 10:31:48 EST 2020 | slthomas
It is strange that you're having issues while using the same process parameters (including stencil) that worked successfully before. It doesn't guarantee that it's not one of those parameters changing in a manner that's not apparent, but it does sugg