Electronics Forum | Sun Nov 16 19:05:45 EST 2014 | warwolf
Seen it. We use a lead free process, sometimes our supplier will use a lead process silk screen that burns at a lower temp. The HASL coat was still SN100CL.
Electronics Forum | Tue Sep 16 17:03:34 EDT 2014 | rangarajd
We have an issue with solder wicking up the leads/ inside terminations on an SMT connector. The solder coverage is sometimes over 50% of the connectors inside pin length. The terminations are gold plated. Is there an IPC spec for acceptability? Plea
Electronics Forum | Wed Dec 10 15:27:14 EST 2014 | sreejhu
Thanks for your reply!! But i dont understand the 300 degree is okay to for lead free process
Electronics Forum | Wed Jan 07 15:48:22 EST 2015 | jacklucas
We switched our PCB's to 170Tg over 10 years ago, so we're probably good to go on the temperature aspect. Thanks for the opinion on the added lead content.
Electronics Forum | Tue Apr 28 16:20:06 EDT 2015 | warwolf
Is this solder lead or lead free? Try look at the delta of the PCB during re-flow, you might find that the smaller parts are being "cooked" faster and burning off the flux.
Electronics Forum | Fri Jun 12 01:17:58 EDT 2015 | armandogomez
hello! Can you be more precise on what you need ? like profiles in general? leaded? lead free? low temp profiles? cheers!
Electronics Forum | Wed Jul 15 12:20:52 EDT 2015 | dyoungquist
If you are using lead solder (SnPb) HASL is a good choice. If you are using lead-free (RoHS compliant) solder then I would recommend Immersion Gold (ENIG).
Electronics Forum | Wed Jan 13 04:07:58 EST 2016 | crystalpcb
Hi Syed, I'm a PCB engineer from China. First:Immersion gold surface finish is the best for PCBs. Second:HASL(Lead-Free HASL) Then:HAL(with lead) The cheapest surface finish is OSP(After 15 days will be oxidized)
Electronics Forum | Wed Sep 09 17:22:42 EDT 2015 | jayrcomajig
Is there any electronic digital devices or other easiest ways to use to determine any unsoldered pins/leads besides some other normal inspections like using microscopes.
Electronics Forum | Thu Mar 02 13:59:38 EST 2017 | horchak
Slim chance it's the nature of the beast if in original unopened package. If handled by anybody not properly trained they will get bent. Allso make sure your pick and place is seating them into the paste, any lead not contacting the wet paste will be
winsouce.jpg)