Electronics Forum | Mon May 18 13:30:15 EDT 1998 | Earl Moon
| I'm reviewing my board fab spec. It calls for a minimum SnPb thickness of 50 microinches on HASL PWB's. I've looked at other specs that call out anything from 30 to 80 microinches, and others that just say the copper pad must be covered and solde
Electronics Forum | Mon Mar 30 07:41:06 EST 1998 | Earl Moon
| Hi, | We have encountered de-wetting issues with gold plated components( SMT LEDs ). | The problem comes and go and we yet to locate the root cause ( process, component or solder paste etc ). | The rest of the components on the boards are not havi
Electronics Forum | Wed Mar 11 11:05:06 EST 1998 | Earl Moon
| I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles mak
Electronics Forum | Sun Mar 15 23:58:01 EST 1998 | Phill Hunter
| | I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles m
Electronics Forum | Thu Jan 15 15:13:50 EST 1998 | justin medernach
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Tue May 21 06:33:37 EDT 2002 | hayashi
*the other components are 0402 and SOIC 16, the > solderability were good. *the protection on the > terminations of microleadframe package is > Cu(copper),somebody call that leadless leadframe > package(LLP). *the time above 210 deg C is about
Electronics Forum | Fri Jun 14 09:15:02 EDT 2002 | edahi
DaveF, Yeah you got that right...because the initial stages of the project, the products would only attach 1 passive (capacitor) hell when things got too cheesy they wanted to attach 20 caps or so....this is not like board assembly, this only 1 Flip
Electronics Forum | Tue Aug 19 09:09:15 EDT 2003 | D Peter
After a few problems and time constraints on baking moisture sensitive devices, we are looking at solutions to storage rather than going after a rebaking solution. One thing that always bothered me about baking was the oxidation on the lead finish,
Electronics Forum | Thu Aug 21 22:10:07 EDT 2003 | adlsmt
Well, for some reason the board house will pay for the boards but has some issue with paying for the parts on them. Why am I not supprised? Perhaps I have mis-diagnosed the problem. We have found two different board p/n's with the same type of defec
Electronics Forum | Sun Aug 29 19:17:34 EDT 2004 | aqueous
Chen, It is always best to place one�s effort on determining the cause and content of the residue rather than trying to work around it. The first thing you must determine is the nature of the residue. Is it flux? In many instances, the residue is