Electronics Forum | Mon Jun 15 16:31:25 EDT 2020 | rgduval
You may find some wetting issues running LF HASL with 63/37, as your reflow temperatures will be significantly below the LF reflow. On fiducials...if you don't have a quote for your boards with ENIG, I would recommend at least checking it out. It's
Electronics Forum | Thu Sep 17 18:22:06 EDT 2020 | astarotf
Hello We have a GSM machine with two heads from the universal company, currently the machine fails to zero and in production mode, when the heads increase the displacement speed in the Y axis, they stop immediately. And the error illustrated in the i
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Fri May 14 07:00:32 EDT 2021 | tommy_magyar
Hi Daisy, I have worked with Viscom AOI before, I am in training with Omron now, but there were many times when this happened to me in the past. Recommended things to do: - Check for duplicated analysis - the AOI might spend time with taking pictur
Electronics Forum | Tue Jul 05 17:09:40 EDT 2022 | madisreivik
PROBLEM SOLVED :) ! I messed with parameters, then started to check hardware again. and.... There are 2 transport position on the carrier 1) vacuum 2) mech clamp Both have fiber position sensor which shows the status When there is component, the
Electronics Forum | Fri Jul 29 06:48:11 EDT 2022 | jojoled
I have old JUKI machine, which after power loss seems to have corupted configuration file(all works fine,except Vision configuration for fiducial recognition : camera is unable to read/ write parameters for Vision), can anybody help to tell which fil
Electronics Forum | Tue Jul 18 16:49:49 EDT 2023 | mahasg
Hello All, I am PhD student at polytechnique Montreal. We have a CQFP44 packages and Dies of 51um pad pitch (22nm FDSOI tech) that I need to bond myself at the university using ASM Eagle Xtreme gold wire bonder in the university. we need to perform b
Electronics Forum | Wed Aug 09 15:06:17 EDT 2023 | SMTA-64386426
The first thing I do when looking at a part relative to stencil design, is determine the coplanarity per the data sheet. Ideally your stencil thickness should be equal to, or if needed, greater than the coplanarity. You want the solder paste to com
Electronics Forum | Mon Sep 25 15:32:21 EDT 2023 | joeljacobo
hello colleagues, Hoping that everyone is doing well, I am reaching out to you in the hope that your experience can help me. We have a wave solder with sac0307 alloy and the pot has turned a golden color, at first I thought it was common tin oxidat
Electronics Forum | Fri Feb 16 09:01:05 EST 2024 | emanuel
I am confused about the parameters of the reflow profile needed to solder lead free components. We assemble boards for automotive modules required with leaded solder paste. The boards have ENIG finish. The problem is that I see some wetting issues, v