Electronics Forum | Tue Sep 11 21:24:00 EDT 2012 | vergara1
I'm also looking for tips for SMT hand soldering > with Sn05Pb93.5Ag1.5. Our technician is quite > good with standard SMT hand soldering, but hasn't > worked with HMP solder. > > Some specific > questions: > > - If the iron tip is hot enough >
Electronics Forum | Thu Jun 21 16:30:47 EDT 2012 | grauen06
We are currently using an ACE K.I.S.S. 104. We used SN100 solder with AIM NC265 flux (no clean, alcohol-based). Also, we use topside preheat at 100 degrees C and a 6mm nozzle (as big as we can go with this application). The PCB has a matte finish as
Electronics Forum | Tue Aug 28 08:28:30 EDT 2012 | rgduval
We agree with all of the previous comments, and would add the following: Warpage is generally caused by excess moisture in the raw boards. Have you tried baking the boards prior to assembly? We had this issue on a simple 4-layer board, and found t
Electronics Forum | Thu Nov 15 10:19:05 EST 2012 | davidmercader
Hi, We have problems with our wave soldering process. The problem is that during the same assembly, after wave soldering, some pcb’s look not clean and other pcb’s look good. We use lead free SAC305 solder and flammable flux. We think our proces
Electronics Forum | Mon Jul 08 13:10:55 EDT 2013 | rgduval
As with any issue like this, your miileage may vary with suggestions....but, here are the items I would consider: 1. Clinch tightness. I believe IPC gives a recommendation on the amount of bend in a clinched lead; make sure you're not beyond that.
Electronics Forum | Wed Aug 21 09:09:50 EDT 2013 | wcheew
I am having solder barrel fill issues on THM component, we follow, we follow IPC 610 E requirement. The barrel fill issues happen on signal & ground pin at connector & E-cap. I found out that most of the insufficient solder happen on the connector ag
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Tue Nov 05 09:57:45 EST 2013 | cuperpeter
Hello All, We have a problem with dewetting of solder paste. Problem is most visible on the pads without components (see attached pictures) and occurs randomly, 20% of PCB's. Pcb supplier sent us a cross-section of pads with thickness of Cu, Ni and
Electronics Forum | Mon Nov 11 08:47:00 EST 2013 | mleber
Thanks guys. Here are more details. The cards are essentially the same. They use the same connectors, same footprint, the traces / layers would be comparable etc. The difference between the 2 we see is that one is laminate - Rigid Metal Clad Base, Ty
Electronics Forum | Sat Nov 23 12:39:18 EST 2013 | joeherz
We installed a Soltec Delta 3 a few months ago and have been trying to run with a VOC free no clean. We're using SN100C in the pot. We are spraying the material and have top/bottom preheat. Evaporation of the water in the flux is a bit of a stru
.png)