Electronics Forum | Tue Jan 23 09:47:02 EST 2018 | dleeper
I've used VJ Electronics Summit series of rework machine. I liked the programing interface. You can used canned scripts for basic removal/replacement processes or you edit/write your own if you want a customized work flow. The machines are very ope
Electronics Forum | Wed Mar 28 11:05:33 EDT 2018 | dleeper
I had a DOS Heller 1500 a looooong time ago so my memory is fuzzy. That being said I remember there were some weird options in some of the configuration menus. I don't remember the names, but its were you would set the alarm points, you could manual
Electronics Forum | Tue Mar 20 05:29:30 EDT 2018 | rob
Fuji makes great machines, just depends on the local support If you are not doing anything special I'd probably just go with the I-pulses as you'll get a lot more machine for your money, and have some left over for inline AOI/SPI or look at somethin
Electronics Forum | Tue Apr 10 02:57:53 EDT 2018 | rob
Yes I would, most of our old Yamaha machines (before 2005) will do 30-35 microns @ 3 sigma with the fine camera option. Our Jukis with His res camera's will hit it too. You should be OK with most things after 1997 with the right camera choice (whic
Electronics Forum | Fri Sep 21 17:33:01 EDT 2018 | michaelszuch
Hello Hai, The first step is to determine where in the process the bubbles are being generated - either during coating or during curing. You can easily check this by letting a few boards air dry (no oven) and comparing them to the oven-cured ones. I
Electronics Forum | Fri Apr 26 05:56:12 EDT 2019 | ppcbs
Check out our line of Shuttle Star BGA Rework Stations. We just sold two model SV560 to a client with the same problem. Our prices include training on machine set up, profile development, process implementation and an operator certificate. We ha
Electronics Forum | Sun Feb 24 11:16:12 EST 2019 | proy
Guys, I have been down this road also spent a lot of time working on this. Electrolytics often are difficult to solder like this. For the sake of testing, try a water soluble more active flux as an initial test. IF you compare hand solder wetting the
Electronics Forum | Fri Apr 26 05:43:50 EDT 2019 | ppcbs
Check out our line of Shuttle Star BGA Rework Stations. Our model SV550 is $18,500.00 installed. Installation includes training on machine set up, profile development, process implementation and operator certificate. We have been providing rework se
Electronics Forum | Thu Mar 28 15:53:49 EDT 2019 | SMTA-Jon
As a CM, we don’t have a lot of input on the PCB layouts we receive. Some engineers/software packages output the paste layer 1 to 1, some do an across the board reduction, and some set each part up individually with different reductions per footprin
Electronics Forum | Tue May 28 18:31:08 EDT 2019 | jlawson
Solder paste flux is main contributor, Lead termination chemical-oxide by products and PCB Plating-Chemicals. Reflow profile would have very limited if not no impact really unless is way off. Paste volume control and Stencil design plays a big part