Electronics Forum | Mon May 25 08:37:28 EDT 2009 | d0min0
Hello, recently we changed supplier of the LF BGA, we did corossection and now have doubts... previous BGA specs : pitch 1mm, ball diameter 0.6mm future BGA specs : pitch 1mm, ball diameter 0.4mm on the crossecrion we found that one of the ball seem
Electronics Forum | Mon May 25 21:10:28 EDT 2009 | padawanlinuxero
Hello !! I have a problem with my wave solder oven, in one of the products we made has connectors on one side of the pcb and in the other one has SMT components the process is kinda tricky on the SMT components we use an adhesive and put to the refl
Electronics Forum | Thu Aug 20 18:11:53 EDT 2009 | smt_guy
Hi davef, thanks again for that enlightenment. I'm just curious about what's happening with the solder joint of the said process. Again to add to my unending queries for now: So on top of that copper is a thin layer of lead-free solder composition
Electronics Forum | Fri Aug 21 04:43:14 EDT 2009 | ghepo
Hello, I suggest you visit the website http://www.analysispcb.com, where I found these information : PARAMETERS FOR DOUBLE “V” SCORING LEAD FREE LAMINATES Typ WEB Thickness, 1.6mm : 0.38mm (+.15/-0) "...Tg is not a good indicator of a materials’
Electronics Forum | Sat Aug 22 05:19:42 EDT 2009 | ghepo
Dear Eric, in my opinion this is a very complex problem, that require to know many details for answer. For example : 1) what about the PCB finishing ? Have you verify the quality of they ? 2) what about the solder paste (the exactly composition)? 3)
Electronics Forum | Thu Aug 27 13:14:49 EDT 2009 | ghepo
I have already told you that is not possible solve this problem by e-mail, without perform a detailed failure analysis. Also I have told you to procede by exclusion. Are you sure, by tests, regarding the PCB quality ? Are you sure regarding the solde
Electronics Forum | Tue Aug 25 03:24:11 EDT 2009 | fiona_j
Hello, I have been recently bringing a new RoHS wave soldering machine into production. Unfortunately, I am finding many of the boards are experiencing blow holes. It is always silver plated PCBs and I believe it is related to moisture ingress. I n
Electronics Forum | Fri Oct 23 08:24:52 EDT 2009 | rgduval
Eric, I haven't used this oven; but, our Heller has built in profiling. Essentially, attach the thermo-couples to a board, and the appropriate point on the oven, and run a board (without parts). Your paste manufacturer will have published a reco
Electronics Forum | Mon Oct 26 13:38:35 EDT 2009 | davef
Type K thermocouples are the most commonly used in the electronics industry. There are various types of thermocouple types that can be used. Examples include [Ray Prasad]: • Type K ¾ nickel-chromium vs. nickel-aluminum (most commonly used); tempera
Electronics Forum | Thu Nov 19 10:24:40 EST 2009 | jeffreyj
I will, though I have to admit that the process thus far has been about as pleasant as getting a tooth pulled. I still wish - as the topic of my thread implied - that there was more information available on production and assembly equipment in the fi