Electronics Forum | Mon Jan 30 13:19:37 EST 2012 | deanm
Now knowing that its a Quad, I'm assuming it has QuadAlign which spins the part it just picked in a beam of light and a sensor measures the length, width and height of each part. If it falls outside of a defined range, it will throw it in the dump bi
Electronics Forum | Wed Aug 15 16:15:51 EDT 2012 | derekj
Hello all. I'm having a bit of an issue with my IVc that's driving me insane. On occasion when placing a part, the machine will consistently reject the part 3 times before adjusting and then pick and place the part with no issues. I've done everythi
Electronics Forum | Tue Dec 26 11:26:00 EST 2000 | acahill
If you have a known problem with the parts, then Reject them back to the Vendor. It appears that you have a solderability issue. As for Tombstoning on 0402 chips, this could trace back to the stencil design and/or machine placement. Define Tombstoni
Electronics Forum | Thu Apr 12 00:43:38 EDT 2001 | zam_bri
Can anybody gimme some input on the problem I faced currently on 0402 Chip Resistor. At pre-reflow the component are placed nicely but at post reflow, we found the Resistor stands sideway ( both termination, the pad and componant are in contact, fun
Electronics Forum | Fri Apr 20 07:30:14 EDT 2001 | wbu
In short: the measured deviation / the length this deviation occurs * 100% = % of deviation Actually we encounter mostly "twist" so we put the board on a flat surface, hold it down at the corners to see if any of the corners lifts, measure the heig
Electronics Forum | Sun Jun 10 23:49:17 EDT 2001 | Robert Sykoh
No-clean is definitely a cheaper process. It will eliminte cleaning. Some issues associated with no-clean are: -- the flux stain left behind on the PCB will create a cosmetic issue. You may want to seek advice from your customers. -- next, the flux
Electronics Forum | Wed Jun 13 21:30:23 EDT 2001 | davef
We use a great concensus document for inspection. It is: IPC-A-610C, Acceptability Of Electronic Assemblies as the basis for accepting assemblies. You can find it at IPC [http://www.ipc.org]. [Help!!!! I�m turning into an IPC Cal.] We find that m
Electronics Forum | Sat Jul 28 05:31:20 EDT 2001 | nop_e
Hi all I just got feedback from my customer about "White residue problem" around solder joints with manaul soldered connector at customer site and included the failure analysis report that there is residues of Cl,S,Na . I 'd like to know, the whi
Electronics Forum | Tue Sep 21 19:09:54 EDT 1999 | Jason Tomlinson
| Does anyone have any figures on what % extra compnents should be supplied on chip components for a particular product build. Typicaly there is wastage due to dropout in loading, 1st board build and machine rejections. Is there any industry standard
Electronics Forum | Mon Sep 27 18:06:26 EDT 1999 | Scott Cook
| Does anyone have any figures on what % extra compnents should be supplied on chip components for a particular product build. Typicaly there is wastage due to dropout in loading, 1st board build and machine rejections. Is there any industry standard
winsouce.jpg)