Electronics Forum | Mon Jan 26 13:13:07 EST 2009 | rgduval
We've had this same problem with the solder wicking to the component terminations. However, in our case, we did not see the pads turning a silver-white color...rather, they exhibited a tarnishing/darkening of the gold. We determined that we had som
Electronics Forum | Wed Mar 04 20:28:17 EST 2009 | kircchoffs
you can copy board at the panelize option and put the value of width of the first board at y of the second board. use panel fiducial at the mark coordinates
Electronics Forum | Mon Aug 17 19:37:25 EDT 2009 | hegemon
And of course the obvious, you'll want to be running that second side on the rail, and not the belt. Yeah, yeah, too obvious, I know... but don't say no one said so! 'Hege
Electronics Forum | Thu Aug 20 07:10:46 EDT 2009 | davef
Questions are: * On what portion of the second side of the board [eg, solder only, solder mask only, etc] do you see this white hazy residue? * Could you attach a picture? * You mention cleaning this residue. What have you used to clean the residue?
Electronics Forum | Tue Aug 25 01:33:00 EDT 2009 | hurr
Hi Jack, we have in our comapany My15 and MY9. Both machines we programming almost daily only in excell. First manually, second with excell macro. Both alternative are almost camparable. It´s depending on amount of SMD parts and skills. Radek
Electronics Forum | Tue Sep 22 08:55:31 EDT 2009 | stepheniii
Second, ESD-stuff > IS very confusing. Largely because people don't > know what they're talking about. I think a lot of that is because of followers following followers.
Electronics Forum | Mon Oct 05 04:55:42 EDT 2009 | pengliang
we suggest as below : the first : check the soldering(solder ball and pad) by X-ray ; second: to do dye analyse (note:pls confrm is there have crack )
Electronics Forum | Wed Jan 06 04:55:41 EST 2010 | deltaservices
Interesting read your tread. I miss one thing, if you want a running garantee, then why not contact a manufactorer for a second hand. Good luck on the new machine, and I hope it will make you a lot of money
Electronics Forum | Fri Nov 13 11:10:07 EST 2009 | isd_jwendell
I'll second the recommendation for the GF-12 series, although I ended up with the Mistral-260 because of the exchange rate and the longer tunnel. Unfortunately the 260 does not open for easy access like the GF-12, although I haven't needed access yet
Electronics Forum | Thu Dec 10 06:01:22 EST 2009 | gregoryyork
have you checked solder resist cure as this will cause the glue to lose adhesion if not cured correctly especially if dwell time sin the wave are excessive i.e 4-5 seconds cheers Greg York
.gif)