Electronics Forum | Tue Oct 26 10:49:00 EDT 2004 | Simon UK
Hi, > > I'm planning to get a new oven. I wanna > know the advantages and disadvantages of each > oven type over each other. I'm being told to go > for an 8 zone oven. > > thanks for your > help. > > regards, Depends really if you want a dua
Electronics Forum | Wed Oct 27 11:38:44 EDT 2004 | marc
This has always been a big debate on what is better. Few things to consider before getting into number of zones. What is the throughput and cooling requirements? Throughput is a direct relation to length of heating zone. Longer heating length
Electronics Forum | Wed Nov 17 09:51:25 EST 2004 | AS
I'm looking for advise on setting up a prototype station for smt (we are currently outsourcing smt production, but have a need for rapid in house prototyping). The station must be able to handle only single sided boards with components no smaller th
Electronics Forum | Wed Jan 05 09:24:53 EST 2005 | cyber_wolf
Well...here is what I can tell you: I have over $40K worth of bent A12,A13,A14 tools.Yes you heard me right $40K worth. (Since 1995) Mydata used to make a repair kit to fix them but decided to quit. They tell me the reason they quit making the kit i
Electronics Forum | Mon Jan 24 18:41:43 EST 2005 | Chunks
Sorry Pete (and others), they do have em'. Back side of the oven. Open the doors with the power supply switch and it's right next to the power relay. Little digital ones on the Omni Flo series. Nope, our company is selling the ovens and several i
Electronics Forum | Thu Jan 27 06:39:59 EST 2005 | reash
For now, on this first board, we will be reworking components such as 0805 and 1210 size caps and resistors, along with SOT-23 and SC-70 size packages. We might eventually get into BGAs. This board will most likely be a double-sided board, probably
Electronics Forum | Tue Mar 15 22:04:56 EST 2005 | KEN
The hasl joint looks fuller (and is easier to inspect)because it has more solder volume. Think about it. Your pre-plating your board with solder (before you add more solder). I doubt your getting 0.3 mils of hasl.....probably more like 1.3 to 3.0
Electronics Forum | Mon May 09 12:26:17 EDT 2005 | stepheniii
If followed, would the following strategy meet the requirements of IPC/JEDEC J-STD-033A; All MSD components are either exposed for less than 1/2 an hour or final reflowed within 12 hours of opening. What I mean by exposed is any time the parts are n
Electronics Forum | Mon May 16 18:03:30 EDT 2005 | davef
Key Issue: Will this machine solder your boards? You never know until you solder one. Any other avenues of analysis involve substantial risk. Flux Selection * High or low solids * VOC or VOC-free Solder Alloy * If using lead-free, avoid stainles
Electronics Forum | Wed May 18 14:58:05 EDT 2005 | splice
Hi, I am having some PTH non wetting issues. Setup and chronology of events is explained: Set Up; Part: 1 MM pitch connector 378 pins Solder: Kester Ultra Pure 63/37 solder Pot; 250 C pre heat; Peak 94C top side Flux: Qualitek 775, Fluxer: foam T
.gif)