Electronics Forum | Wed May 21 08:16:57 EDT 2008 | tonyamenson
Good morning gentlemen, I could use some advise as to the min / max windows for the wave process. We have had little problems with our leaded wave but when applying the same process to lead-free wave we are having problems. Obvisouly the temps are
Electronics Forum | Wed May 21 13:59:19 EDT 2008 | pjc
Here's what I've seen for no-clean flux applications: Leaded: Dwell Time is? 2 - 3 seconds Top side board temp max? If some small SMT parts reflow are we too hot? 110 to 120C top side board temp just before hitting the wave(s) Pot temp. 245C Lea
Electronics Forum | Tue Aug 19 13:35:51 EDT 2008 | stefi
Hello, I need an advice regarding the next issue: in the case of Assembleon Topaz or Emerald SMT machines, is there necessary to teach first the block repeat coordinates and after that the PCB fiducial coordinates when you do not have these coordina
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Mon Dec 22 20:16:17 EST 2008 | davef
The first question in solving the "ol' SMT component loss after second-side wave operation" problem is: So, what makes you think the components actually came-off in the wave and not during some previous 'handling'? Putting that aside, we'll play thi
Electronics Forum | Wed Dec 24 11:23:22 EST 2008 | childs
I can't seem to locate any information/concerns about moisture entrapment in IC packages on the promary side in a double sided SMT assembly using water soluable solder paste when soldering the second side. A typical process would assemble/reflow/cle
Electronics Forum | Thu Feb 12 11:57:59 EST 2009 | jmiller
i have searched the forum for hours. read all the threads that deals with cleanliness and ionic testing. (http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=40295) (http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=22603) (http://www.
Electronics Forum | Fri May 22 12:42:43 EDT 2015 | deanm
Sr. Tech, you are right in that there is no verification of the profile. We are a Class 3 high mix OEM. We have visual inspection after SMT. We have not seen problems with wetting, grainy solder, cold solder, charred boards, etc. that would indicate
Electronics Forum | Thu Jul 01 16:02:45 EDT 2021 | willkillum
Greetings. Make sure the calibration/homing chip is still with the machine and not lost, although you can buy a replacement from Juki for a not-so-nominal fee. Also, have the seller power it up and bring up the Laser image display/edge check. If ther
Electronics Forum | Wed Feb 10 05:23:17 EST 2021 | karl_willoughby
Hello. I am sourcing machines for an SMT line (for the first time) and would like to understand features of current and earlier model SPI and AOI machines. In the intended application, a high volume of PCAs aren't required to be processed but there
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, China
Phone: 0755-33578694