Electronics Forum | Fri Jul 29 08:22:34 EDT 2011 | mskler
What will be the specifications of solder paste printing for 6 mil thikness in SnPbAg process. Also what will be the control limits fro X bar R chart. Thanks in advance for the help
Electronics Forum | Fri Jan 16 15:41:23 EST 2004 | patrickbruneel
David, You just provided enough material to start an endless debate in an unexplored field (acceptable impurities, levels and effect on reliability in high tin content (lead free alloys). High tin content alloys have a high affinity to metals like C
Electronics Forum | Fri Oct 09 15:06:22 EDT 1998 | Chrys
Dave F asked me for an update on the SRS we evaluated last month... I like this machine. Over 80% of your wave dross is actually good solder; you just can't get to it without some type of separating agent. I like the mechanical sepration method mu
Electronics Forum | Fri Oct 09 16:33:08 EDT 1998 | Dave F
| Dave F asked me for an update on the SRS we evaluated last month... | | I like this machine. Over 80% of your wave dross is actually good solder; you just can't get to it without some type of separating agent. I like the mechanical sepration met
Electronics Forum | Tue Dec 12 13:45:23 EST 2000 | justin m
Dross removal is dependent upon the "activity" in your solder pot and the usage of a inert or an "air" atmosphere. The more moving parts that agitate the solder and expose it to air, the more dross. Basics first and then the answers will make sense
Electronics Forum | Sat Jun 12 19:08:11 EDT 2004 | Ken
Well, it finally happened. A machine Operator did not follow our bar code process and "grabbed a tube of solder paste" and guess what. Built 250 assemblies with LF paste when it should have been Tin/Lead!!!! SOLDER PASTE SUPPLIERS: can you make t
Electronics Forum | Tue Dec 15 17:01:36 EST 1998 | Chrys
| Does anyone know what a TCP is? | What type of process is required for assembly, what type of equipment? | | Any help or resources on the subject would be greatly appreciated.. | | Thanks | Brain, TCP, or tape carrier package is the same as TAB
Electronics Forum | Wed Jun 16 14:05:23 EDT 1999 | Dave F
| A potential customer of our is inquiring if we have capability | for Hot Bar manufacturing in the PCBA manufacturing world. If someone can explain to me what this entails, I would greatly appreciate it. Thank you. | Gary: Tell your customer NO
Electronics Forum | Fri May 16 11:19:23 EDT 2003 | blnorman
In addition to the information provided above, we put a bar code label on each of our PCB's, and on 4 lines we burn in the bar code with a laser. That way we have traceability on that board throughout our process. At the end of the line another bar
Electronics Forum | Thu May 30 10:45:16 EDT 2002 | sjpence
We got a similar alloy Sn05Pb93.5Ag1.5, of Alpha Vaculoy bars. It is not the eutectic alloy you were looking for but it is close. This alloy and similar high temperature alloys are used in downhole electronics and so a supplier in the Houston area