Electronics Forum | Fri Aug 20 12:41:20 EDT 1999 | stefano bolleri
| | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | This is what I did. | | | | Created a removal pr
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Thu Aug 05 11:51:44 EDT 1999 | Wolfgang Busko
| | | | | | | | | | | | Hello, | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem with chi
Electronics Forum | Tue May 18 15:36:18 EDT 1999 | Tony
| | | What is the best way to re-ball a BGA? Who has the best system for doing it? | | | | | I'm using our SRT rework stuff to reball in house - when necessary. Of course, we only do this for protos and test boards. We use a standard micro-stencil,
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Fri Mar 19 11:01:42 EST 1999 | Dave F
| Hi folks, | | I am looking for inputs on a long-standing problem encountered in our shop: Bottom-side parts (passives) falling off in the Wave...where the only remnants of the part is a flattened glue dot of proper diameter and volume, and somet
Electronics Forum | Mon Dec 13 00:48:33 EST 1999 | armin
Hi All I have a 0.7 mm diameter hole for vias, what�s the minimum annular ring for this hole diameter? What�s the term unsupported and supported holes refer to in IPC-2221 9.1.2 Annular Ring Requirements? I have a proto-type PCB (designed by our R&
Electronics Forum | Tue Jun 29 04:45:10 EDT 1999 | Earl Moon
| | Hey there gang, how's it going ? | | | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my componen
Electronics Forum | Thu Jun 03 14:40:22 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W
Electronics Forum | Thu Jun 03 14:41:06 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W