Electronics Forum | Mon Oct 04 07:47:34 EDT 1999 | park kyung sam
| | What are pro's and con's of reflowing top side first and curing bottom side chip components, and then wave soldering bottom side? | | | | How about curing bottom side first and reflowing top side later? | | | | What percentage of companies run
Electronics Forum | Tue Sep 22 13:14:27 EDT 1998 | Chrys
| We are getting into a lot of double sided boards offlate. Our customer is loading a lot of RNETS, Diodes ( MINLS, SOT23s and other 2 leaded diodes ). We are processing it through a traditional glue process and wave soldering the SMT parts along wit
Electronics Forum | Wed May 26 14:24:13 EDT 1999 | Boca
| | we have just started wave soldering passive SMT components and through hole. We are having trouble with voids on the SMT components. It is very random, but effects a lot of TSOT's. We are using an electrovert with a chip wave. Are there any o
Electronics Forum | Mon Apr 26 09:46:05 EDT 1999 | C.K.
Chrys: I have checked all the basic elements of Wave solder joint formation: fluxing, preheating, and lastly soldering. For checking the fluxer, i used a product from ECD that's very similar to what you desribed called the flux-o-meter. It did a
Electronics Forum | Mon Jul 05 03:14:47 EDT 2004 | P.V
I am looking for the solder pot size on the above wave machine, any help would be appreciated
Electronics Forum | Thu Feb 14 12:44:48 EST 2008 | operator
Don't worry about the paste print. Just omit it from the stencil. Mask over all the SMT components after reflow with water washable WSOL masking. Then run it thru the wave to deposit the solder. Then wash to remove masking. Or you could manually run
Electronics Forum | Mon Feb 06 19:11:25 EST 2012 | broncomania
Yes. You need to educate your customer... On a side note, hopefully these boards hasn't gone through wave over your LF solder pot.. This will contaminate your solder pot and won't be cheap to fix it.
Electronics Forum | Sat May 14 03:56:40 EDT 2005 | Mika
I am interested in RoHS "through-hole soldering": We have a problem with solder wetting and fillet during selective and wave soldering, with a Ni/Au PCBA!! Different fluxes has been tested, but this is really a big issue. Now; there is only a few fl
Electronics Forum | Wed Sep 29 23:54:07 EDT 1999 | Dreamsniper
Hi everyone, Greetings! I�ve got a 2-layered through-hole PCB�s having the following problems: Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB Insufficient Solder and some solder never make it to t
Electronics Forum | Wed May 27 09:56:39 EDT 1998 | Chrys
| | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localize