Electronics Forum | Wed May 03 22:41:36 EDT 2006 | ramerez
I am based in Nogales and I have also tried the MS2, I was told to immediately cancel my trials, It did reduced the build up of dross but the mess it made to the wave and the surrounding areas was very bad, Everything was coated black and the smell a
Electronics Forum | Wed Dec 06 16:27:35 EST 2006 | mscalzo3
We would be able to help you in any way that we can. There was an article in SMT magazine that explains a lot. Also, we have data on other processes that have successfully done this conversion. This has been a popular way of eliminating the conver
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Sat Apr 21 15:50:14 EDT 2007 | GS
Hi, which kind of stainless steel are made your solder pot components? for istance : AISI-304 ? AISI-306 ? AISI-312 ? AISI-316 ? As we know AISI-316 will last more against Tin erosion. But AM SACX does not allow so much !!! I know who since t
Electronics Forum | Tue May 29 05:00:41 EDT 2007 | lococost
Grant, apart from troughput another thing to consider is boarddesign, If there is any SMD within a diameter (eg 3mm) of the connector you won't be able to solder them. I think those are the 2 main disadvantages of selective. That being said, for le
Electronics Forum | Thu Nov 08 12:05:05 EST 2007 | jdumont
Hole size may not have been an issue for you because your holes were already big enough? The alloy you are using has a lot to do with this I believe also. We are already at 5 seconds dwell for this which is mfg recommended for our solder. The caps we
Electronics Forum | Mon Nov 26 15:24:12 EST 2007 | joeherz
A recent thread regarding the ACE KISS equipment has me wondering if anyone is happy with their choice in selective equipment. I don't see much mentioned about Pillarhouse, Juki, ERSA and some of the others. We're currently debating whether to inve
Electronics Forum | Tue Dec 18 09:44:51 EST 2007 | bbarton
CC True enough, indisputable and factual...my whole point was that there was NO communication from the company(s) or the peddlers on the subject, causing an unimaginable number of wave operators, engineers, production managers and CUSTOMERS to pull o
Electronics Forum | Fri Jun 20 14:03:33 EDT 2008 | wavemasterlarry
LiSten my Consultancy Firm has branched out into all matters not just wave related but related to any type of production processees. I myself not only consult in a wavemaster soldering expert role but also am willing to work in an operator type of ca
Electronics Forum | Thu Apr 07 04:32:13 EDT 2011 | jacki
Dear All During SMT process, some Tant caps were fell down without touching Epoxy . I found the problematic Tant Termanations were bended with gap. So I called to Vender and expalined this gap but the answer was the gap was within their standard and