Electronics Forum | Fri Jun 06 13:03:01 EDT 2014 | asksmt
Hi All, i have footprint 2X5 RA HEADER 2MM spacing in design. I am using about 9 mils of annular ring on top side and about 12 mils of annular ring on bottom side. refer picture attached. we are having solder short issues during wave solder so was
Electronics Forum | Sun Sep 21 15:48:48 EDT 2014 | gascon5383
Our company has a process standard that requires a double person check at the beginning of every run (size of run is irrelevent, whether 20 panels or 500 panels). Every changeover that occurs a first piece inspection is made before reflow. If all is
Electronics Forum | Mon Nov 10 09:03:47 EST 2014 | rgduval
I can't claim to be an expert....I've just bought a used RPS, and it'll be my first...but, after reading through their manual, and working on setting things up, I'd say: -Conceptually, I like the idea of moving the board rather than moving the entir
Electronics Forum | Fri Nov 21 11:00:27 EST 2014 | gregp
Hi J_Dub (Joe), Thanks for the input. Sounds like some fairly densely populated through hole assemblies. 100 solder joints per board is up to 50 parts per board (I know you may have DIP's so it could be less than 50). 24 boards in a panel x 50 par
Electronics Forum | Wed Feb 11 17:04:47 EST 2015 | davef
A-610E, 10.7.4 covers solder mask discoloration. Use that for your disposition In a previous thread, Boardhouse told us "Here are a couple of things that can affect color. * Material color is the major, * Matte green from Enthone would be different
Electronics Forum | Tue Feb 17 12:58:11 EST 2015 | anvil1021
The MV-7 OMNI is a Great Machine, has the same 3D Solution MV-9 Quad Moire Multi Frequency System. You will not be disappointed, you will find new ways to use the 3D system as time goes on and it is rock stable and incredibly precise. Either the MV-
Electronics Forum | Tue Feb 17 09:33:43 EST 2015 | emeto
Hello, I have two of these for the last 3 years(MV-7xi). Buy the machine with the best camera they offer and with the telecentric lens - it gives great view and resolution. I had to replace the controller for conveyer open/close on both of them. I a
Electronics Forum | Wed Mar 11 17:32:46 EDT 2015 | jlawson
Small paste deposits have less flux thus less flux activity to enhance the wetting. So preheat needs to be as short as possible, ramp to spike if possible. Try not to ramp hold and spike - pending thermal delta on product can be made to ramp to spike
Electronics Forum | Fri Mar 06 07:15:38 EST 2015 | saoasasd
Hi, I have faced some problems with DQFN PACKAGE 132 PIN. After some cross sections and dye pry analysis we could find a head on pillow situation always on inner row pads. The PCBAs are double side and the DQFNs are assembled on Bottom side (Noteboo
Electronics Forum | Tue Mar 10 04:36:41 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si