Electronics Forum | Thu Jul 20 23:41:55 EDT 2017 | heros_electronics
Below is an email that I copy and pasted from my customer's engineer about his concerns with the issue of the chips not reflowing (which is why I was asking about X-ray the chips to make sure they reflowed): Can you let me know your thoughts on his
Electronics Forum | Wed Feb 14 16:58:12 EST 2018 | cbart
you would be best to get this from your paste/solder manufacture. but here are some rules of thumb: -Solder paste out of fridge before use - get out the night before needed.. don't let your op's warm on the oven!! you will regret that! if not over ni
Electronics Forum | Thu Dec 03 21:40:01 EST 2020 | itmconsulting
Hey Kyle - Good for you for pushing your horizons and considering pin-in-paste (aka "Intrusive Soldering"). Don't let the nay-sayers out there discourage you. When I encounter mixed tech PCBAs (SMT and through-hole) my first choice, if the design a
Electronics Forum | Fri Mar 10 09:01:44 EST 2000 | Wolfgang Busko
Hi John, we had one shot with silver coated PCBs. With "no clean" and no changes in process parameters ( we had no input on necessary changes from the boardhouse ) we encountered wetting problems in the first reflow soldering process. Later it was s
Electronics Forum | Wed Mar 01 17:05:34 EST 2000 | Dave F
Glenn: I hear you, but when Steve talks about a "dark haze" and "scrap(ing) the �black stuff� off the pads" to make them solderable, but I don�t think of "black pad." I think of "black pad" as a surface coating that typically can not be removed by
Electronics Forum | Wed Mar 01 16:58:03 EST 2000 | Dave F
Robert: On your balls: Solder suppliers make several "standard balls" and can advise you. On your cleaner: Recycling water / direct to drain? Most batch cleaner suppliers can advise you on recycling and filtering systems to keep you out of troub
Electronics Forum | Fri Feb 25 04:28:49 EST 2000 | Sze-Pei LIM
We faced terrible void issue while using Sn96.5Ag3.5 solder paste, more than 20% void. We tried adjusting the reflow oven profiles but we did not have much success in reducing the void. Generally, we find quick preheat, high peak temp. and fast cooli
Electronics Forum | Wed Feb 23 21:23:56 EST 2000 | Larry Johnson
Does anyone know where I can find something in writting on the proper ways to clean a mis-printed board using no-clean solder paste? If not, can any of you tell me what the best way is? Currently, we are running mis-printed boards though the Aqueou
Electronics Forum | Tue Feb 22 11:53:16 EST 2000 | JAX
Sal, To answer your first statement; Yes, you can cure paste and reflow solder using one profile. Question on your second statement; Are you talking about running passive side glue, flipping it over, running active side solder, and then putting the
Electronics Forum | Thu Feb 17 21:42:12 EST 2000 | Dave F
Hey Bud: Moved from that Bi-crap to something serious, eh? Several things: 1 Get in touch with Doug Romm (drom@msg.ti.com) at Texas Instruments. He talks palladium. 2 Review the archives on Palladium. 3 I think you're running light on temps. Eut